EDAX

The phase composition, microstructure and the element of the thin film were characterized respectively with X-ray, scanning electron microscopy and EDAX.

通过x射线衍射仪、扫描电镜、能谱分析仪分别对（Ti，Al）N薄膜的相结构、微观形貌及薄膜成分进行了检测与表征。

By means of SEM 、 EDAX and OM, the petrographic structure and microscopic chemical composition of cement clinker have been researched by adding rare-earth lean ore.

采用SEM、EDAX、OM等分析测试方法，研究了稀土贫矿掺加条件下，水泥熟料的岩相结构及其微区化学组成。

Only Bi exists in the deposit by EDAX, and is metal crystal with average size 38 nm by XRD.

用EDAX分析镀层确认只含铋，用XRD对镀层进行表征，证明了镀层中的铋以金属晶体存在，平均粒径为38nm。

the thermal degradation and antiwear mechanism of zddp are detailed by means of ir, ms, nmr, edax, friction and wear testers of mm-200 and mq-800 four ball.

通过红外光谱仪、质谱仪、核磁共振仪、能谱仪及MM-200摩擦磨损试验机、四球机等技术手段，分析了二烷基二硫代磷酸锌热分解产物组成及其抗磨机理。

The morphological structure of moggy guard fur was observed by SEM. The elements in squama, cortex and medulla were also analyzed by EDAX.

本文对家猫针毛的形态结构进行了扫描电镜（SEM）观察，并且利用X射线能谱仪（EDAX）分别对鳞片层、皮质层和髓质层进行了元素分析。

The solid solution of Sr _ ( 1-x ) Ca _ xCuO _ 2 is investigated by means of XRD, EPMA and EDAXmethods.

本文用XRD 、 EPMA、EDAX等 方法,研究了Sr_ ( 1-x ) Ca_xCuO_2固溶体.

The influence of α-Al2O3 micropowder additions on permanent linear change, apparent porosity, cold crushing strength and slag resistance of MgO-Al2O3 based castable is studied in this paper. By EDAX analysis, the mechanism of slag corrosion is investigated.

研究α-Al2O3微粉加入量对钢包渣线用镁铝质浇注料线变化率、显气孔率、耐压强度和抗渣性能的影响，借助EDAX分析，探讨了浇注料的渣蚀机理。

To know the current status of airborne pollution in Yungang Grottoes, main substantial composition of the deposition of airborne particles is analyzed by means of XRD, SEM ( EDAX), and microscope.

为了解云冈石窟大气中粉尘污染的现状，用X射线衍射、扫描电镜（EDAX）和显微镜对大气中粉尘的主要物质成分进行了分析。

The component of second phases was analyzed by EDAX.

通过EDAX对第二相化学成分进行了定性分析。

Analyses of EDAX show that sealing white line was glass spreading on oxide scale of pin.

EDAX分析表明,封接白线是销钉封接时玻璃沿销钉氧化膜的爬坡.

The joint structure and element distribution at brazing seam are also studied by SEM/ EDAX and thermodynamics measures.

通过SEM/EDAX以及热力学方法分析了钎焊接头组织及钎缝的成分分布。

EDAX analysis indicated that the interfaces phase included high content of Y and Al.

EDAX分析表明界面相是钇、铝含量很高的物相；

The microstructure of Ni-P chemical deposited coating layer on 45 steel has been studied using TEM, EDAX and X-ray diffraction method.

用透射电镜、能谱仪及X射线衍射法研究了45钢化学沉积Ni-P镀层的微观结构。

The composition and structure of film were studied by means of EDAX and XRD.

用能谱仪和XRD研究了膜层的成分和结构。

The profile of metal ions in Masson pinewood is researched by means of SEM EDAX and atomic absorption spectrometer. The content and retentivity of metal ions in unbleached KP AQ pulp of pinewood are studied.

用扫描电镜能谱仪（SEM EDAX）及原子吸收光谱仪研究了马尾松的金属离子分布及马尾松硫酸盐蒽醌（KP AQ）法未漂浆中金属离子的分布及滞留性能。