inoculant

The influence of inoculant addition amount on the structure and properties of camshaft was investigated.

试验了孕育剂量对凸轮轴组织和性能的影响.

Too high addition amount of the stream inoculant is easy to cause inclusions, slag and inoculant cluster which would lead to the formation of hard spots.

随流孕育剂加入量过高容易产生夹杂物、夹渣缺陷，还会发生孕育剂聚集引起的硬质点。

And for secondary inoculation, high efficacy complex inoculant is added into hand ladle in amounts of 0.1%~ 0.2%.

在手端浇包内添加w为0.1%~0.2%高效复合孕育剂，进行二次孕育；

New Approach for Rhizobial Inoculant Production Using Industrial Sludge

工业污泥用于根瘤菌菌剂生产的新方法

Application of Inoculant-RSC to Grey Cast Iron

RSC孕育剂在灰铸铁中的应用

Natrium molybdate was not suitable to be added into rhizobial inoculant, because of the low viable number and its high effect on pH ( value).

钼酸钠对菌肥的活菌数和pH影响大，钼酸钠不宜作为钼肥添加到根瘤菌剂中。

The influence of SG inoculant on graphitizing annealing of malleable cast iron was investigated.

研究了SG变质剂对可锻铸铁石墨化退火的影响.

The effect of increase soybean production by silicate bacterium inoculant

硅酸盐菌剂对大豆的增产效应

The first part took temperature, moisture, pH and C/ N ratio as the main technological index to make sure the befit compost condition of quantity of inoculant, moisture, pH and C/ N ratio.

第一部分以温度、水分、pH值、C/N比为主要研究技术参数，通过这些参数确定适合畜禽粪便高温好氧堆肥的VT菌剂的接种量、水分条件、pH值条件及C/N比条件。

some techniques to improve the mechanical properties of v process castings, such as surface alloying, inoculant addition to the coating are presented.

也介绍了改善V法铸件机械性能的方法，如表面合金化，涂料中加入孕育剂等。

The Inoculant Used for the Grey Iron with High Si/ C Ratio

高硅碳比灰铸铁用孕育剂

Microscopic examination of the spent filters revealed that even when the inoculant pellet failed to completely dissolve, the reaction products were still retained within the filter.

通过对用过的过滤器的微观检测显示，即使在孕育块未能完全溶化的情况下，反应产物也仍能保留在过滤器上。

the effect of using compound inoculant bacteria on ensilage of corn and alfalfa

利用青贮复合菌剂制作青贮饲料的效果测定

The results also show that it is necessary to restrict Si of base iron within 1.2% in order to control graphite degeneration and improve mechanical properties, when the base iron melt is treated with 1.8% nodularizer contained Y and 0.4% inoculant contained Ba.

当钇基重稀土球化剂和含Ba孕育剂加入量分别为1.8%和0.4%时，原铁液硅含量控制在1.2%以内，有利于防止厚大断面球墨铸铁件石墨畸变，提高铸件力学性能。

Inoculating effects of the inoculant have been evaluated by experiments of section sensitiveness and inoculation fading.

通过断面均匀性试验和孕育衰退试验检验了多元复合孕育的效果.