inorganic adhesive

The compression shear strength of dowel joint of YW-1 inorganic adhesive is 140-180 MPa.

YW-1无机胶用于套接粘接，套接压剪强度可达140-180MPa。

Bond forming tests including organic binder, calcium, inorganic adhesive series pilot; preparation of composite adhesive for bonding test; use coking coal and organic binder mixed with coke test.

粘接成型试验包括对有机粘接剂、钙系列的无机粘接剂进行试验；配制复合粘接剂进行粘接试验；选用主焦煤与有机粘接剂混合用型焦试验。

Experimental investigation on fatigue life of the YW-1 copper oxide-phosphate inorganic adhesive with 45 steel specimen was conducted. The S-N curve was obtained.

本文对磷酸氧化铜无机胶进行了套接抗拉疲劳寿命的试验研究，测出了该胶的S-N曲线及疲劳极限。

This paper inquired into deeply the reason for being high strength in the puffing-inside adhesion of YW 1 inorganic adhesive from the Chemical, physical and mechanical.

本文从化学、物理、机械三方面深入地探讨了YW-1无机胶套接粘接形成高强度的原因。

Inorganic adhesive H3PO4 CuO is presented for replacing phenol aldehyde resin adhesive in preparing diamond grinder.

采用无机粘结剂H3PO4CuO取代酚醛树脂粘结剂，制作树脂磨具。

test study on shear strength of polycrystalline diamond bonded with copper oxide inorganic adhesive

氧化铜无机胶粘接聚晶金刚石时压剪强度的试验研究

Investigation on Torsional Sheath Strength of Dowel Joint of Copper Phosphate A Study on Modified Cupric Oxide-Phosphoric Acid Inorganic Adhesive

磷酸氧化铜无机胶套接扭剪强度研究