cordierite的例句大全

A catalyst carrier of composite type was prepared by nickel wire and porous cordierite ceramics. The binding technology between metal matrix and porous ceramic coating was studied, and properties of the coating material were measured.

通过金属镍和堇青石多孔陶瓷制备了复合型催化剂载体，探索了多孔陶瓷涂层与金属基体之间的结合工艺，测量了涂层材料的相关性能。

Structural States 、 Sintering Temperature and Thermal Expansion of Cordierite

堇青石的结构状态与合成温度、热膨胀的关系

Effect of different raw materials and synthesis temperature on the thermal expansion coefficient of synthetic cordierite

不同原料及合成温度对合成堇青石膨胀系数的影响

A deep blue cordierite often used as a gemstone.

一种深蓝色的堇青石，用作宝石。

The test results show that: By holding time is 6 hours at 1330 ℃, performances of synthetic cordierite by the 4# recipe are better, and the cordierite samples have low thermal expansion and content of synthetic cordierite is most.

本试验研究结果表明：采用4配方经烧成温度为1330℃，保温时间为6小时后合成堇青石的常温指标较好，而且该试样具有较低的热膨胀性、合成堇青石的含量较高。

The thermal spalling resistance of the cordierite glass ceramic is governed by various factors such as cordierite content, visual porosity rate, sintering schedule and etc.

堇青石微晶玻璃抗热震性能受堇青石相含量、视孔隙率、烧成制度等多方面因素的影响，该陶瓷热震次数最多达到26次。

Moreover, high-temperature thermal storage materials with improved thermal shock resistance and increased thermal storage capacity are prepared by doping in-situ synthesized cordierite with silicon carbide, zirconium oxide and mullite.

在原位合成堇青石基础上，通过添加碳化硅、氧化锆、红柱石、莫来石及采用原位合成莫来石方法进一步提高堇青石材料的抗热震性能和储热性能。

Cordierite ( MAS) and MAS/ SiC multiphase material were prepared, and then the multiphase material's bulk density, open porosity, flexural strength and thermal-shock resistance were measured.

合成堇青石（MAS）并制备MAS/SiC复相材料，测试了复相材料的体积密度、开口气孔率及抗热震性等。

research shows that the heat reflectance of the compound outer wall heat-insulated paint prepared with the tbh emulsion as base, 10g hollow glass micro-pellet and 2g cordierite as fillings reaches 91.67%.

研究发现：以TBH为成膜基料，添加10g空心玻璃微珠和2g堇青石填料，制备出的复合型外墙隔热涂料的热反射率达91.67%。

mas precursor powders are prepared using aluminium sulfate, colloidal silica, and magnesium nitrate as raw materials via sol-gel methods, dsc-tg and xrd show that the mas precursor powders transform to cordierite completely at 1300 ℃.

以硫酸铝、硝酸镁和硅溶胶为原料，采用溶胶-凝胶法，制得MAS先驱体粉末，XRD表明，该粉末经1300℃的热处理后，完全转变为堇青石。

The feasibility of manufacturing one-fire cordierite push bat brick for kilns burning porcelain by using chamotte, sintered magnesia clinker and special grade bauxite as starting materials has been expounded.

阐述了以低铝熟料、烧结镁砂、特级高铝矾土为原料制备的堇青石为基质.一次性烧成陶瓷窑用推板砖工艺的可行性。

adding 7% cordierite, 7% flint clay and 2% quartz sand in matrix enabled the castable to have highest thermal shock resistance.

基质中同时引入7%的堇青石、7%的焦宝石和2%的石英砂时，浇注料的抗热震性最好。

solid phase reaction process of cordierite powders prepared by sol-gel method and its sintering

溶胶-凝胶法制备堇青石粉体的固相反应过程和烧结性的研究

this article introduced the conditions of testing and using the saggar which made from sillimanite and cordierite .

本文主要介绍了硅线石、堇青石复合材质匣钵的试验和使用情况。

monolith catalysts were prepared for methane combustion by using ysz, y-al2o3 or oxygen storage ( osm) materials as supports, fe, co, mn as activity components and cordierite honeycomb ceramics as substrate.

本文以YSZ、γ-Al2O3及储氧材料为载体，以Fe、Co、Mn为活性组分，用堇青石蜂窝陶瓷为基体制备了整体式甲烷燃烧催化剂。

The best scheme: The raw meal to the cordierite grog is 7:3 . 3.

混合坯料中性能最佳的方案是生料: 熟料二7:3.

The crystallization of the stoichiometric cordierite was studied by using TG-DTA and XRD.

采用TG -DTA 、XRD分析了理论化学组成的堇青石微晶玻璃的晶化行为.

It is found that homogeneous, dense and single-phase C 0.6 M 0.4 ZP coating was successfully deposited on cordierite ceramic.

结果表明,在堇青石表面制备的涂层均匀致密,由 单相 的C0.6M0.4ZP组成.

Light-coal Cordierite is widely used as inner insulating lining for air stove, furnace, coke oven, pit.

堇青石质煤轻砖用于热风炉 、 加热炉 、 焦炉 、 均热炉内衬隔热保温.

The present invention a ceramic material preparation process, and relates a cordierite honeycomb ceramic preparation process.

本发明属于陶瓷材料制备工艺, 涉及堇青石蜂窝陶瓷制备工艺.