Theo outlook of studies on the rapidly quenched amorphous superconducting alloys

急冷非晶超导合金的现状与展望

Technological Test for Improving the Impact Toughness of Quenched and Tempered Steel Forgings

提高调质钢锻件冲击韧性的工艺试验

It was also found the synthetic mechanical properties of the samples quenched in air at1000 ℃ became excellent when temper temperature was460 ℃.

对于1000℃空淬试样，在460℃回火处理时可获得较好的综合力学性能。

Low temperature electrical resistance behaviour in rapidly quenched Amorphous Ni-B alloys

急冷非晶合金Ni&B的低温电阻行为

The results show that the microstructures are related to the attenuation coefficients. Among pearlite plus ferrite, quenched martensite, and tempered martensite, α of pearlite plus ferrite is the biggest, α of tempered martensite is the smallest.

实验结果表明，对于珠光体+铁素体、淬火马氏体及回火马氏体3种组织，珠光体+铁素体的超声波衰减系数最大，回火马氏体的最小；

Sulfide Shape Control in Non Quenched and Tempered Steel Containing Sulphur

含硫非调质钢中硫化物形态的控制

Surface Microstructure and Properties of Quenched and Tempered Steel by High Current Pulsed Electron Beam

调质钢电子束表面处理组织及性能分析

Material Impact of the Factors on Quenched and Tempered Steel Welded Joints Toughness

调质钢焊接接头冲击韧性影响因素分析

Manufacture of large mixed model spherical tanks with domestic High-Strength Quenched and tempered steel

用国产高强度调质钢制造大型混合式球罐

Research for Changing Shroud and Deformation of Middle Carbon Quenched and Tempered Steel Impeller

中碳调质钢叶轮换盖盘变形的研究

Dry Sliding Friction and Wear Characteristics of MoSi_2 against 45 Quenched and Tempered Steel

MoSi2/45~钢在干摩擦条件下的滑动摩擦磨损性能

Behavior of H_2S Stress-corrosion for Quenched and Tempered Steel of Pressure Vessel Steel

压力容器用调质钢的H2S应力腐蚀行为

At the same tempering time and tempering temperature, as the quenching temperature rise, the corrosion resistance of the samples decreased. But under quenched at 930 ° C for 30 minutes, the best comprehensive performance can been obtained.

随着淬火温度的增加，相同的回火温度与回火时间的试样的力学性能在930°C淬火时达到最高，而耐蚀性能则不断降低。

The superplasticity of the as sprayed and twice oil quenched specimens were examined and their tensile elongation with 119% and 328% were obtained, respectively.

选取喷射成形铸态及经过二次油淬超塑处理两种状态试样进行拉伸试验，得到伸长率分别为119%和328%。

Fractography of the quenched tensile specimen under cycling treatment changes from dimple pattern to mixed fracture with dimple and tear ridges.

循环温度场作用下淬火态合金拉伸试样断口由韧窝型断裂向韧窝和撕裂棱混合型断裂转变。

After thermomechanical treatment, the natural quenched alloy has coarser precipitates and its distribution is inhomogeneous.

热轧后经自然冷却的合金经热机械处理后，析出相粒子较大，分布也不均匀；

The rectifier filter's circuit is developed through current design and parameters optimization, the surge current is quenched and the AC voltage is transferred into high DC voltage to supply the DC/ DC converter.

通过电路设计，参数优选，研制了整流滤波电路，使开机浪涌电流得到了抑制，把交流电变换成了高压直流电，供给DC／DC变换器；

The effect of preheating treatment process of cold rolls on induction heat quenched structures and the effect of heating temperature and time on structure and hardness have been studied.

研究了轧辊的预备热处理工艺对感应加热淬火组织的影响，感应加热温度和时间对组织和硬度的影响。

The experimental results in detecting the time-resolved fluorescence of dipeptide and quenched fluorescein by the self-constructed system are also presented.

同时，具体给出了利用自行搭建的频率上转换系统探测双肽和淬灭荧光素时间分辨荧光的实验结果。

These steels are aged hardenable martensitic steels. The superior combination of strength and toughness is achieved through precipitation of fine M_2C alloy carbide by quenched and aged treatment.

该类型钢是一种时效硬化马氏体钢，通过淬火和时效处理析出弥散细小合金碳化物M＿C，达到强度与韧性的最佳配合。