austenite的例句大全

The thermoplasticity in a high temperature plastic zone was good because of the deformation twin formed in austenite grains.

在高温塑性区塑性良好是由于奥氏体晶粒发生大量的孪生变形；

According to austenite isothermal transformation diagram, a heat treatment process for producing the left and right pincers through fixed heating time and the position was put forward.

借助奥氏体等温转变曲线，创立了定时定位的热处理工艺方法，用于左右钳口的生产，一次达到设计要求，简便可靠，省时节能。

This article studied the welding processing of ring board and round belt for round belt container made of austenite stainless steel through welding experiment, reasonable welding methods and processing parameters are worked out.

本文通过焊接试验对奥氏体不锈钢绕带容器环板与绕带焊接工艺进行了研究分析，并得出了合理的焊接方法和工艺参数。

The electronic structure of austenite of high strength and high toughness steel was investigated by the recursion method in the tight binding approximation.

在紧束缚框架下用Recursion方法计算了高强高韧钢中奥氏体相的电子结构。

The results showed that the deformation induced ferrite inverse transformed to austenite and grains growted within holding time after deformation.

结果表明，在变形后的保温过程中，形变诱导的铁素体先逆相变为奥氏体，同时伴随着诱导铁素体晶粒的长大；

The main problems found in the production of austenite stainless steel reactor are analyzed in this paper, and at the same time the solution methods are given.

本文重点分析了有关奥氏体不锈钢反应器加工制造过程中的一些关键问题及其处理方法。

Influence of antimony on secondary dendrite arm spacing of primary austenite of Hypoeutectic grey iron

锑对亚共晶灰铁初生奥氏体二次枝晶臂间距的影响

The influence of tin precipitation on austenite grain size in titanium microalloyed steel

微钛钢中TiN析出对奥氏体晶粒长大的影响

Influence of Pouring Temperature on Primary Austenite in Semi-solid Hypoeutectic High Chromium Cast Iron

浇注温度对半固态亚共晶高铬铸铁初生奥氏体的影响

The microstructures change of super-high strength of austenite stainless still silk in multi-ply drawing were analysed.

分析了超高强度奥氏体不锈钢丝在多道次拉拔过程中的组织变化。

In 20th century, we applied the thermal stabilization of austenite in order to reduce the deformation during quenching for steel parts ( during tempering for high speed steel).

在20世纪，我们在热处理中应用奥氏体热稳定化，有效地减小淬火（高速钢回火）时钢件的畸变。

Influences of carbon, silicon and aluminium on reaction on surface of austenite stainless steel powder during sintering

碳、硅和铝对奥氏体不锈钢粉末烧结时表面反应的影响

At last, the density of dislocation of the material increases greatly after hot forging, then segregation of carbon occurs, which also result in non-uniformly austenite and then spheroidal pearlite.

热加工时，位错密度大大增加，使碳出现偏聚，增加了奥氏体不均匀的程度，促进粒状珠光体的形成。

Study on the Mechanism of the Austenite of Inhomogenous Carbon Concentration in Spheroidizing Annealing

奥氏体碳浓度不均匀在球化退火中作用机理的研究

The spheroidizing annealing tests were carried out on the 1.6% C forged UHCS ( ultra-high carbon steel) based on DET ( Divorced Eutectoid Transformation) mechanism of the austenite with inhomogeneous carbon concentration. The mechanical properties of the UHCS samples with different microstructures were tested.

根据碳浓度不均匀奥氏体的离异共析转变机制，对1.6%C（质量分数，下同）锻造超高碳钢进行不同工艺的球化处理，并对具有不同球化组织的试样进行性能试验。

The microstructure of austenite in the worn surface layer of Fe C Cr Mn cast iron sliding against 800# SiC sand paper was observed with a transmission electron microscope ( TEM).

用透射电镜观察了Fe-C-Cr-Mn亚稳奥氏体基铸铁在800SiC砂纸上经往复摩擦磨损试验后磨损表层的微观结构。

Effect of sliding velocity on the frictional behaviors of in situ granular eutectics reinforced austenite steel matrix composites

滑动速度对团球共晶体增强奥氏体钢基自生复合材料摩擦学性能的影响

It is proved by the experiment and practice that the stability and hardenability of the austenite have slight effect on the properties of the metallic material during the process of the laser surface strengthening.

试验和实践证明，在激光表面强化的过程中，奥氏体稳定性和淬透性对金属材料性能的影响不是致关重要的；

Uneven Factor and Control of Austenite Grain Growth of Tool Steels

不均匀因子与工具钢奥氏体晶粒长大的控制

The results show that the hypereutectic structure, which contained alloy carbides ( Cr7C3) with the hexagonal or stripy feature and with the wavy boundary and had a martensite matrix with a small amount of austenite, performed the best abrasion resistance.

试验结果表明：堆焊合金中具有波形边界的一次六角形或条状碳化物（Cr7C3）、且基体为大量马氏体加少量奥氏体的过共晶组织抗磨料磨损性最佳；