The shape of A-type and B-type crystallite is basically spherical, and their diameter is 2~ 10 μ m. Their relative crystallinity is 80% and the polymerization degree ( DP) of peak values is 14~ 19.

实验中所得A-型和B-型微晶的相对结晶度为80%左右，外形多数为球形，直径一般在2~10μm之间，峰值聚合度DP在14~19之间。

Besides, at certain spinning speed and pump delivery the crystallinity increases with the increase of spinning temperature but the orientation degree decreases.

在一定纺速和泵供量下，结晶度随纺丝的温度的升高而提高，取向度则下降。

The results showed that the crystallinity and crystal orientation degree of PET combined filament yarn were increased when the heat godet and heat plate temperatures were elevated. The heat godet temperature had a slight effect on the crystallinity at high heat plate temperatures.

结果表明：随着热盘温度和热板温度的提高，涤纶混纤丝的结晶度和晶粒取向度有所提高，在热板温度较高时，热盘温度对结晶度的影响较小。

A study on the crystallinity of sericin by X-ray diffraction

用X射线衍射法对丝胶结晶度的研究

The influence of glass fiber, flame retardant and nucleating agent on the crystallinity and mechanical properties of polyethylene terephthalate ( PET) was investigated.

研究玻纤、阻燃剂和纳米成核剂对聚对苯二甲酸乙二酯（PET）结晶性能及力学性能的影响。

Measurement of the crystallinity of synthetic molecular sieves& three point method

合成分子筛中分子筛含量测定方法&三点高度角度差乘法求衍射强度比

The conclusions of XRD and FT-IR experiments showed that, the nitrate radical hydrotalcite, prepared by the co-precipitation method, whose crystal form is stable, and crystallinity is so good, then the sodium styrene sulfonate organically-modified hydrotalcite was prepared by the ion exchange method.

XRD和FT-IR结果表明：采用共沉淀法较好地制备得到了硝酸根型的水滑石，晶形稳定，结晶度好，而利用离子交换法制备了对苯乙烯磺酸钠修饰水滑石。

The results show that, core shell impact modifier can act as nucleation agent, which can increase the crystallinity of nylon 11 blend alloy.

实验结果显示，核-壳冲击改性剂具有成核剂的作用，有助于共混体系结晶度的提高。

The crystallinity reach its peak when the content of epoxy is 1%, with the increase of epoxy resin content, the crystallinity of nylon 11 alloy decreases.

环氧树脂用量为1%时，尼龙11共混合金体系的结晶度最大，此后随着环氧树脂的加入，尼龙11结晶度随之降低。

The solubility was a function of solubility parameter, polarity and crystallinity of VDC-AN-St terpolymer;

实验表明，溶解度是溶度参数、极性和共聚物结晶度的函数；

Sediments illite crystallinity measurements showed that the ancient humid climate had gradually changed from the evolution of drying.

沉积物中伊利石结晶度的测量结果显示了古气候由湿润逐渐变为干燥的演化规律。

The size of crystalline region and relative crystallinity were measured by X-ray on the timber which was treated by PF resin. The measurement results show that the crystalline structure of cellulose baldly changed compared with untreated wood.

利用X射线衍射法测得PF预聚物处理材的晶区大小和相对结晶度，结果表明，PF预聚物的引入没有改变纤维素的结构。

The experiment results of crystallinity in some organic solvents showed that there was a strong tendency to spontaneous nucleation in the solution of OGO.

对OGO在多种有机溶剂中的结晶性能进行了研究，结果表明在实验的几种有机溶剂中OGO的成核趋势很强，在甲苯和苯中具有较好的结晶特性。

The crystallinity of fiber increased with the rise of stretching temperature.

结晶随拉伸温度的升高而增加。

The neat arrangement of molecules, high crystallinity and high stiffness makes ramie fiber fabric feel itchy to skin.

苎麻纤维由于分子排列整齐、结晶度高、刚度大，故导致苎麻织物在穿着过程中产生刺痒感。

ftir spectra showed that maillard reactions occurred between cmc and spi, and xrd scans indicated that the maillard reactions greatly reduced the crystallinity of spi.

红外光谱分析发现，CMC与SPI之间发生了美拉德反应，XRD也证明上述反应可大大降低共混材料的结晶程度。

Using a gangue as raw in the experiment, the process of synthesizing gangue-based adsorbent with high crystallinity and purity by self-transformation of gangue in vapor phase of ethylamine and water at a temperature range of 373~ 400 K was researched.

以煤矿的废弃物煤矸石为原料，研究了373~400K温度范围内，煤矸石在乙胺和水的蒸汽相中自转变合成纯度、结晶度均较高的矸石基吸附剂的过程。

The experiments include wear test, crystallinity test, coefficient of thermal expansion test, DSC test and PV limit test.

对烧结试样进行了摩擦磨损实验、结晶度分析、热膨胀性能分析、DSC热物理性能分析和极限PV值测定。

The influences of content of nucleating agent on crystallization peak temperature, crystallization curve shape, crystallization onset temperature and crystallinity of co-polypropylene were studied in detail by means of DSC.

用差示扫描量热仪（DSC）详细研究了成核剂用量对共聚聚丙烯的结晶峰温度、结晶峰形、结晶起始温度和结晶度的影响。

The influence of reactive compatibilizers on the crystallinity and nucleating of PA6 was examined with the use of differential scanning calorimetry ( DSC).

用差示扫描量热仪（DSC）研究了接枝改性聚烯烃弹性体POE对PA6结晶度的影响。