curing temperature的例句大全

When curing temperature was preferred to be 260 and the percentage of solidification agent was 3 %.

固化剂质量分数为3%,固化温度为260℃时得到的膜的性能最佳.

Come through the curing temperature by differential scanning calorimetry ( DSC), Curing trial in combination with curing reaction appropriate curing time.

通过差式扫描量热法（DSC）得出固化温度，并结合固化试验得出固化反应适宜的固化时间。

In order to determine reasonable processing parameters, heating of thermosetting molding compound in the mold and that of heat transfer after curing temperature are analyzed.

本文就模压料在模具中加热过程和达到固化温度以后的传热过程进行定量分析，以确定合理的工艺控制参数。

However, the high benzoxazine resin curing temperature, low cross-linking density of the cured product, brittle and other defects restrict its application in some special fields.

但是，苯并恶嗪树脂固化温度偏高、固化产物交联密度偏低、性脆等缺陷制约了其在一些特殊领域的应用。

Moderate curing pressure and curing temperature were beneficial to composite properties.

适中的固化压力与固化温度有利于材料具有较好的力学性能与导电性能。

Determination of Curing Temperature and EV Time for Thick walled Rubber Article

橡胶厚制品硫化温度与等效硫化时间的测定

with curing time and post-curing time increased, the compression set was improved. reasonable choice of curing temperature and curing time, can make vulcanized rubber with good comprehensive performance.

合理选择硫化温度和硫化时间，可使得硫化胶具有较好的综合性能，采用二段硫化能提高硫化胶的力学性能，二段硫化时间为2h时综合性能较佳。

The customer can use OPP by standard thick film printing process with curing temperature 200 ℃.

采用厚膜印刷工艺，200℃固化。

The experimental results show that the curing temperature of the modified MDPES for making the composite mainly depend on both the reaction of network formation and the cleavage of the ether linkages in BE.

研究表明，选择BE/MDPES的固化温度时，必须同时考虑网络的形成反应和BE中醚键的断裂反应。

The key consideration and the pouring temperature of the concrete under low temperature construction, curing temperature, heat storage and holding time parameters on the maximum temperature rise inside the concrete, as well as the size of the surface tensile stress, and draw some useful conclusions.

重点考虑和阐述了混凝土在冬季施工下的浇注温度、养护温度、蓄热保温时间等参数对混凝土内部最高温升以及表面拉应力大小的影响，得出了一些有益的结论。

Curing Effects of Automatic Controlled Temperature and Forced Humidified Air Exhausting Apparatus

烤烟自动控温强制排湿装置的烘烤效应

This also improves the stability of the HIPE and expands the temperature range for pouring and curing this HIPE during subsequent emulsion polymerization.

它还提高了HIPE的稳定性，扩大了在随后的乳状液聚合中倾倒和固化该HIPE的温度范围。

Then, it makes target mixture proportion design to study on the aggregate gradation scope, optimum asphalt content of mixture, the temperature and time of curing.

然后，对确定配合比例的国产环氧沥青进行混合料目标配合比设计，确定了矿料的级配范围、混合料的最佳油石比以及高温固化温度、时间等参数。

Phenolic aldehyde epoxy resin exhibits high radiation reactivity, and its high temperature modulus and glass transition temperature ( Tg) after curing is higher than that of bisphenol A epoxy resin.

酚醛型环氧树脂辐射反应活性高，固化后的高温模量及玻璃化转变温度高于双酚A型环氧树脂，但固化度沿辐射深度方向下降较快。

The results showed that, the higher temperature in earlier curing stage could accelerate the reaction speed of blended cement and increase the reaction degree, but it would affect the increase of reaction degree in later standard curing stage.

研究结果表明，早期较高的养护温度可加快混合水泥的反应速率，提高其反应程度，但对后期标养条件下混合水泥反应程度的增长有影响；

Coil coatings was thermal analyzed and researched with DSC in order to test glass transition temperature ( Tg) of the paint film at the maximum precoated metal temperature ( PMT) and determine the optimal curing conditions of different coil coatings.

采用DSC进行卷材涂料热分析研究，测试在不同PMT（最高金属板温）下漆膜的Tg，以确定各种卷材涂料的最佳固化条件。

High temperature curing of unformed plate in valve-regulated lead-acid battery

阀控铅酸蓄电池生极板的高温固化

Combined with seedling technique research achievements on other plants, adequately utilizes the existing tobacco facilities, seedling-raising technique by improving temperature and fill-in light in the curing barn.

本文结合其他植物补光育苗技术的研究成果，利用现有的烤房设施，以缩短育苗期，培育苗壮为目的，在烤房中进行增温补光育苗。

Exothermic reaction can lead to higher local temperature composite materials, which form a complex temperature gradient, the results will lead to non-uniform curing.

放热反应可以导致复合材料局部温度较高，而形成复杂的温度梯度分布，结果将导致非均匀固化。

The cure kinetics of DGEBA/ Dicyandiamide ( DICY) system was investigated under temperature programming curing condition. Differential Scanning Calorimetry ( DSC) was the thermo-analytical technique used to determine the cure kinetics of this system.

采用程序升温差示扫描量热仪（DSC）法研究了DGEBA／双氰胺（DICY）体系的非等温固化反应动力学。