metallographic的例句大全

Fractured translation cam of motor planet reducer was studied by chemical analysis, hardness test and metallographic examination.

介绍了电机行星减速器动凸轮的断裂情况，对断裂动凸轮进行了宏、微观检验。

The brazing of aluminium alloy 6063 on different thermal parameters in air furnace with proper technical measures was tested. The appearance of the hazed ioints and the metallographic microstructure as well as the shearing strenth were checked and analysed.

采用不同加热制度在空气炉中进行6063铝合金的钎焊试验，并对钎焊接头进行了外观、金相及剪切强度的检测分析。

The analysis of fracture failure for loom barrel arbor was explored with macroanalysis, microanalysis and metallographic inspection method. The result indicates that barrel ardor fracture is belong to fragile shear fracture without any obvious fracture portent, fracture may be caused by moment impact overloading.

通过宏观和微观的断口形貌观察和金相分析，对织机卷筒轴断裂失效原因进行了分析，认为卷筒轴断裂属于无明显断裂前兆的脆性剪切断裂，断裂有可能由瞬时冲击过载引起。

Highly ordered porous anodic alumina template was prepared by twice anodic oxidation in acidulous electrolyte, and its morphology was observed by metallographic microscopy.

在酸性电解液中，用二次阳极氧化法制备得到了高度有序的多孔阳极氧化铝模板。

We can manufacture metallographic samples by hands or the polishing machine.

金相试样的制作可以手工完成，也可以通过抛光设备来完成。

Their metallographic structures were qualitatively and quantitatively analyzed by scanning electron microscope and X-ray diffraction method. And the relationships among heat treatment parameters, content of retained austenite and carbon content of retained austenite were studied.

通过电子扫描电镜及X射线衍射仪对其金相组织进行定性、定量分析，研究热处理参数与残余奥氏体体积含量、奥氏体含碳量的关系。

With the same surfacing parameters, the metallographic structure, hardness, resistance to tempering and abrasive resistance of the deposited metal were compared and analyzed.

在堆焊工艺参数相同的情况下，对微观金相组织，宏观硬度、抗回火性及耐磨性的研究，分析比较了两种药芯焊丝堆焊熔敷金属的力学性能。

Metallographic Essence of Hydrogen-induced Disbonding of Stainless Weld Overlay

不锈钢堆焊层剥离断裂的金属学本质

Metallographic Problems of the Materials for Fossil Power Unit

火电机组材料的金属学问题

appearance performances include drape pendency, stiffness and crease recovering, etc. the hardness tester can be equipped with camera device, it can take photos of tested indentation and material metallographic composition.

服装的外观性能包括悬垂性、硬挺度、折痕恢复性、起毛起球等方面。硬度机可选配摄影装置，能对所测压痕和材料金相组织进行拍摄。

Metallographic theory and analysis have been proved the rationality of ancient and current technology for making variegated copper.

就斑铜的历史、古代和现代班铜技术、用金属学理论分析了获得宏观大斑花的依据、证明了古代和现代斑铜工艺的合理性。

A metallographic analysis of the spay-welding layer

喷焊层金相分析

The Electropolishing and Preparation Process of Titanium-alloy Metallographic Specimen for OIM Testing

钛合金材料OIM试样的电解抛光及制备工艺

FES-DP mainly consists of four modules: the module of operation parameters and materials database, the module of metallographic photos, the module of the equipment operation rules and the assessment module.

FES-DP系统主要包括加热炉运行参数及炉管数据模块、金相组织图谱模块、装置管理条例模块和评估模块四个模块。

Metallographic Structure Process and Analysis System Based on Microsoft Office Software

基于Microsoft Office的金相图像采集、处理与分析

The fine blanking dies of the pawl and the chute used for the seat recliner were firstly introduced in this thesis, and failure analysis has been carried out in view of mechanical calculation, metallographic test, hardness test and SEM.

本文首先针对棘爪、滑槽板两副精冲模具出现断裂的凸模，从力学强度校核、金相试验、硬度试验、断口电镜扫描等进行试验分析。

Chemical composition, hardness, microstructure and pitting defect appearance of the failed bearing rolling elements were studied by methods of chemical analysis, hardness testing, scanning electron microscope and metallographic examination.

采用化学分析、硬度测定、扫描电子显微镜检查和金相分析方法，对失效轴承滚动元件的化学成分、硬度、显微组织和滚动道（面）上的点状缺陷的形貌特征进行了分析。

The CCT curve of the bainite transformation of the Mo bearing and Mo free trial steel has been measured and the metallographic structure of the steels observed by expansion method in a thermo-simulation machine.

在热模拟试验机上采用膨胀法并结合金相组织观察，测定了含钼和不含钼的试验钢贝氏体转变CCT曲线。

The variation of hardness and precipitation behavior during aging at 525 ℃ after relaxation in deformed Nb-bearing microalloyed steel were studied by thermo-simulation test, metallographic analysis, measurement of hardness and TEM.

采用热模拟手段、金相及硬度测量并结合透射电子显微镜观察，研究了简单成分的含Nb微合金钢在热变形弛豫后、525℃时效时硬度变化及析出过程。

The microstructure evolvement of bainite under different relaxation time after deformation in austenite for microalloyed steel was studied by applying thermo-simulation test, metallographic analysis, semi-quantitative measurement and PTA technique.

利用热模拟、金相分析结合半定量测量统计及径迹显微照相技术（PTA），研究了微合金钢奥氏体区变形后弛豫不同时间的贝氏体组织演化情况。