It was found that the best conditions for preparing nickel hydroxide nanorods were the reaction temperature in the range 180~ 200 ℃ and the pH value between 9 and 10.

结果表明，氢氧化镍纳米棒形成的最佳条件是180～200℃，pH为9～10。

The measurement results of XRD and TEM indicate that the crystallization of the nano scale nickel hydroxide is β form and its shape is spherical with a diameter of 30~ 60 nm.

XRD和TEM测试结果表明：样品为球形或椭球形，直径30～60nm，晶型为β型。

The Effect of Ethanol on Electrochromic Properties of Hydrous Nickel Hydroxide Films

乙醇对含水氧化镍薄膜电色特性的影响

Nickel hydroxide is the positive electrode active material of Ni-MH battery.

氢氧化镍是Ni-MH电池的正极活性物质。

New Development in Preparation of Nanometer Nickel Hydroxide Used As Cathode Material

电池正极材料纳米氢氧化镍的制备新进展

The physical properties of nickel hydroxide samples such as tap density, particle surface shape, particle size and distribution and flow ability were investigated to confirm above conclusion.

并对Ni（OH）2产品的堆积密度、表面形貌、粒度及粒度分布及流动性等物理性质进行了表征。

The nickel hydroxide with tap density> 2.1g/cm 3 and discharge capacity> 270mAh/ g is prepared by the most efficient process which was determined by many experiments.

在实验中确定了反应的最佳工艺，使氢氧化镍的堆积密度＞2.1g／cm3，放电比容量＞270mAh／g。

Company spherical nickel hydroxide nickel-hydrogen batteries are the key raw materials, technical superiority prominent.

公司球形氢氧化镍是 镍氢 电池的关键原材料, 技术优势突出.

cobalt was deposited on spherical nickel hydroxide by electroless plating, using hydrazine or sodium hypophosphite as reductive agent and ammonia or potassium sodium tartrate as complexing agent, respectively.

采用水合联氨或次亚磷酸氢钠作还原剂，分别在酒石酸钾钠和氨的配合体系中镀覆球形氢氧化镍，对一定金属钴镀覆量下的产物进行了XRD和SEM分析与观测。

the investigate to purifying nickel sulfate for producing nickel hydroxide

氢氧化镍生产中硫酸镍的提纯研究

Nickel hydroxide are widely used as an active material of positive electrode in alkaline rechargeable battery.

氢氧化镍作为碱性蓄电池的正极活性物质被广泛应用.

Companies are hydride battery cathode material of spherical nickel hydroxide Asia, one of the main suppliers.

公司是镍氢电池正极材料球形氢氧化亚镍的主要供应商之一.

However, B-nickel hydroxide is a low conductivity P-type semiconductor.

但是球型氢氧镍是P型的半导体, 放电容量不高.

as in a nicad battery, the nimh's anode is made of nickel oxyhydroxide immersed in an electrolyte of potassium hydroxide.

就像镍镉充电电池一样，金属氢化镍电池的阳极是由浸泡在氢氧化钾电解质中的羟基氧化镍制作而成。