sintering temperature的例句大全

Effect of reactive sintering temperature on properties of Si_3N_4-SiC refractories

反应烧结温度对Si3N4-SiC材料性能的影响

Coercive force decreases with the increase of the sintering temperature.

磁体的矫顽力随着烧结温度的升高单调下降。

There are a minimum value of the porosity and a maximum value of the thermal conductivity in the sintering temperature range.

在烧结温度范围内随着气孔率出现最小值时，导热系数出现最大值。

Its optimum sintering temperature is 1550 ℃, holding time 1. 5h.

其最佳烧结温度为1550℃，1.5h。

Study on the Sintering Temperature Speciality of GH 30 alloy Wire Netting Material

GH30合金丝网材料烧结温度特性的研究

The favorite conditions of preparing oxygen cathodes are that the mass ratio of graphite: acetylene black: activated carbon is 1 ∶ 1 ∶ 1, the sintering temperature of the cathode is 400 ℃ and the thickness of the cathode is 1 mm.

电极的较佳制备条件为：石墨、乙炔黑与活性炭的质量比1∶1∶1，烧结温度400℃，电极厚度1.0mm；

Structural States 、 Sintering Temperature and Thermal Expansion of Cordierite

堇青石的结构状态与合成温度、热膨胀的关系

The comparison shows that the thermal etching carried out at a temperature lower than the sintering temperature can obviously reveal the grain structure of Al_2O_3 matrix. The metallic particles after thermal etching were not moved away from the samples, as normally occurred in chemical etching.

比较表明，在低于烧结温度约150℃下进行的热腐蚀能够清晰地揭示基质Al2O3的晶粒结构，并且与化学的效果不同，保留了金属相粒子。

With the decrease size of powder, not only will the sintering temperature range fall, but also there is no air pores in the ceramics. 5.

随着粉料的粒度的减小，不但获得理想烧结状态所需的烧结温度范围随之降低，而且消除了显微气孔。

The optimum preparation condition was that sintering temperature was 1215 ℃ and holding time was 45 min.

磁体的最佳烧结条件为：温度1215℃，保温45min。

Relation between Sintering Temperature of Cathode Blocks and Versus Oxygen Concentration in Electrolytic Tantalum Powders

阴极块烧结温度与电解钽粉氧含量的关系放电等离子烧结制备铁基大块非晶材料

The sintering temperature and thermal expansion coefficient of the LSGM sample were determined using dilatometer.

用热膨胀仪确定了LSGM的烧结温度及热膨胀系数。

With increasing sintering temperature, the joint of graphite and BN was increased and also there was transition layer in the interfaces relative to HP.

随着烧结温度的升高，元素扩散加剧，过渡层的厚度越厚，材料的层间界面结合强度升高，石墨层与BN层结合的越好。

Study of the Relation Between Electromagnetic Parameter and Sintering Temperature of Low Loss Mn-Zn Ferrite

低损耗Mn-Zn铁氧体电磁参数与烧结温度的关系研究

The methods to modify the volatility amount of organic vehicle were proposed, and the volatility data are useful for the reference of the sintering temperature schedule of electronic paste.

提出了调节有机载体在不同温度下挥发量的方法，可为电子浆料烧成温度制度提供参考。

Porous silica ceramics with low density were successfully fabricated by a novel tert-butyl alcohol ( TBA)-based gel-casting method. The effects of solid loading and sintering temperature on the microstructure, phase, pore size distribution and physical performance were studied.

研究了不同固相含量和烧结温度对制备二氧化硅陶瓷显微结构、性能、物相以及孔径分布等方面的影响。

The Influence of Sintering Temperature in NiO Target on the Properties of Exchange Coupling NiO/ Ni_ ( 81) Fe_ ( 19) Double Layered Films

NiO靶烧结温度对NiO/Ni（81）Fe（19）双层膜的影响

The density of sintered pellets increases with the sintering temperature at constant sintering time and the increment of the sintered-pellet density with the sintering temperature is much more significant than that with sintering time.

在相同的烧结时间内，提高烧结温度，烧结块的密度随之提高，且提高程度比延长烧结时间提高的程度更为显著。

High sintering temperature and long maintaining time lead to the sufficient crystallization and the full densification, but result in the worsening of the deviation from the stoichiometry.

高的烧结温度和长的保温时间使结晶更加充分，样品致密度更好，但是也造成偏离化学计量比的加剧。

In the most appropriate range of sintering temperature for feldspathic ceramics, sintering time should be prolonged appropriately ( 5 hours) to increase the content of leucite crystals.

长石瓷有一最佳的烧结温度范围，在此范围内，适当延长保温时间（5小时）有利提高长石瓷中白榴石的含量。