And the thermotechnical calculation solution of the solidification heat transfer device was attained.

总结给出了凝固换热装置的热工计算方法和计算机进行求解的逻辑框图。

solidification heat transfer process and control for secondary cooling zone of slab casting

板坯连铸二冷区凝固传热过程与控制

The processing method for latent heat releases in alloy castings is introduced by the combination of the temperature recovery and the equivalent heat capacity, which can be applied in alloy solidification of any temperature range with the high efficiency.

通过温度回升法与等效热容法的结合，提出了一种能够处理铸件凝固潜热释放问题的方法，它可适用于任意结晶温度区间，且计算效率很高。

The movement of phase-change interface, the heat flux rate of the boundary, and the relationship of the thickness of slab and the predicted time of solidification under different cooling conditions were obtained.

获得了该蓄冷介质在板式蓄冷器中凝固时的相界面移动速度，边界面热流密度随时间变化的规律，及不同工况下蓄冷板厚度与预测蓄冷时间的关系。

A composition coating for ferrous metal alloy surfaces was comprised of phosphates base solution, heat-resisting pigments and some additives, which could be solidified on the surface of plain steel in ambient temperature without solidification agent.

研究了一种用于钢铁表面的磷酸盐复合涂料，它由复合磷酸盐基液、耐热颜料和一定的添加剂组成，涂刷在普通钢铁表面上可在室温自然固化。

Instability of flow due to complex heat exchange and density variation leads to strong thermal convection in liquid region during the water solidification process. At the end of solidification process, intensity of flow decayed and the stable structure was rebuilt.

因为存在着复杂的热交换和密度变化，水在凝固过程中存在流动结构失稳，使得液相区内发生强烈的热对流.最后流动强度减弱，重新形成稳定结构。

The Quality Control of Round Cast Alloy Production Numerical Simulation on Heat Transfer and Solidification of Coupling Graphite Sleeve with Round Cast Iron Bar in Horizontal Continuous Casting

铸造合金棒裂纹分析与控制铸铁水平连铸中结晶器和型材传热凝固的耦合数值模拟

Numerical Simulation of Flow and Heat Transfer in Inverse Solidification Mold

反向凝固结晶器中流动与传热的数值模拟

A mathematical model for heat transfer in course of CC round billet solidification was established.

建立了一维非稳态连铸圆坯凝固传热数学模型。

The calculated results could preciously and correctly reflect the characteristics of non-uniform heat transfer around the mould circumference, which provided an applicable method for applying numerical simulation technique to monitor the solidification process and the "visual mould" technology in continuous casting.

计算结果准确地反映了实际生产过程中沿结晶器周向非均匀传热特征，为将数值模拟技术应用于连铸凝固过程监控和可视化结晶器技术提供了可借鉴的实用方法。

The experimental results show that tung oil on the surface of the compound fertilizer granules after heat solidification forms a continuous envelope with good adherence, and tung oil-coated compound fertilizers with a coating rate of 10.1% have 80% of their nutrients released in 27 days.

实验结果表明，桐油在复合肥料颗粒表面经热固化后形成连续和附着良好的包膜层，包膜率为10.1%的桐油包膜复合肥料的80%养分释放时间可达到27d。

taking angang heavy slab continuous caster as the target machine, solidification and heat transfer mathematic models for continuous casting second cooling zone are established according to heat transfer theory.

以鞍钢厚板坯连铸机为目标机型，按照传热学理论建立连铸二冷凝固传热数学模型。

the concept of effective heat capacity is introduced to deal with the latent heat source term from phase transformation. during the programming for computation, the dynamic updating method is also applied to simulate the influence of solidification on physical properties.

同时利用有效热容的概念来处理相变潜热源项，在程序编制过程中利用动态更新来实现凝固对物理量的影响。

The heat of fusion is equal to the heat of solidification.

熔解热等于凝固热.

The heat transfer in continuous casting of Tin was calculated with this model, it was found that temperature of initial solidification area was varied periodically along with mold oscillation.

在此基础上，模拟了结晶器振动条件下的锡液初始凝固传热行为，发现锡连铸中，初始凝固区域温度随结晶器振动而发生周期性变化。

An explicit finite& difference method ( FDM) was used to model and simulate the solidification of eutectic cast iron by combining heat transfer equations with undercooling nucleation and growth laws.

综合热传导方程与过冷形核、生长规律，用显式有限差分法模拟了共晶铸铁的凝固过程。

Based on the temperature recovery method, a new model is presented to handle the latent heat release of gray cast iron during the solidification process of both primary solidification and the eutectic solidification stages.

基于潜热处理的温度回升法，针对灰铸铁凝固过程中具有初晶和共晶两个阶段的凝固特性，提出了适合灰铸铁的带共晶的潜热处理方法。