To adopt welding procedure method commonly used in long distance transmission pipeline, analog field site condition to weld for pipe with SSCC resistance itself and carry out SSCC resistance test to girth weld jointer obtained to provide technical support for oil and gas construction.

采用目前长输管线常用的焊接工艺方法，对本身具有抗SSCC性能的钢管模拟野外现场条件进行焊接，将所得环焊缝接头进行抗SSCC性能试验，为油气管线的施工建设提供技术支持。

SSCC is typical low stress tardy crack.

应力腐蚀是典型的低应力滞后断裂。

In addition, based on detailed analyses of test results and careful observation of corrosion tests, this thesis discussed the protective mechanism of coatings resistant to SSCC and the failure mechanism of some kinds of coatings in wet H2S environment.

同时本文在对试验结果详细分析及对腐蚀试验过程仔细观察的基础上，论述了涂层防止湿硫化氢应力腐蚀的防护机理，以及几种涂层的失效机理。

The inspection on bare tube, which included chemical composition, mechanical property, hardness and corrosion resistant test such as SSCC, HIC, Intergranular Corrosion, all the results were up to the standard.

对成品管进行化学成分、拉伸性能、硬度等性能和抗硫化物应力腐蚀开裂、氢致开裂、抗晶间腐蚀性能检测结果均合格。

The results suggested that different welding material match leads to different resistance to SSCC.

不同的焊接匹配将导致管线钢具有不同的耐腐蚀性能；

Effects of band structure on SSCC and CO 2 corrosion

带状组织对SSCC和CO2腐蚀的影响

The control measures must be completed before a further SSCC is issued.

必须完成控制措施后才重新签发船舶卫生控制措施证书。

Test Methods and Technique of Sulfide Stress Corrosion Cracking ( SSCC) Occurred on Steel

钢铁发生硫化物应力腐蚀裂开的试验方法与技术

The Influence of Cold Work of Austenitic Stainless on Martensite and SSCC

奥氏体不锈钢冷加工与形变马氏体及耐应力腐蚀的关系

The SSCC is valid for a maximum period of6 months.

船舶卫生控制措施证书最长有效期为6个月。

SSCC low differentiation, cancer cells small, granular nuclear chromatin, cell shape is similar with the SCLC.

SSCC分化较低，癌细胞较小，核染色质呈颗粒状，细胞形态上与SCLC有相似之处。

Sulfide hydrogen stress corrosion cracking ( SSCC) is the main factor to restrain the application of the pipeline steels.

硫化氢应力腐蚀破裂（Sulfide Stress Corrosion Cracking，SSCC）是制约管线钢应用的主要因素。

The mechanism and general influence factors of sulfide stress corrosion cracking ( SSCC) of chemical equipment made of high strength steel are summarized.

系统的综述了高强钢化工设备硫化物应力腐蚀开裂机理及常规的影响因素。

The more quantity of sulfur and inclusion in the steel, the lower the resistance of the steel to SSCC.

钢中硫含量和夹杂物的增加，可使钢的抗硫性能下降。

The result showed that the microstructure dominated by fine and homogeneous acicular ferrite had the better resistance to SSCC.

结果表明：均匀细小的针状铁素体为主的显微组织具有优良的抗SSCC性能；

The analysis results indicated that the H_2S in the LPG caused sulfide stress corrosion cracking ( SSCC) of the flange.

分析结果表明，法兰断裂是由液化气中的H2S所引起的应力腐蚀开裂。

The results demonstrate that the SSCC sensitivity of 16Mn ( HIC) increases with increase of hydrogen sulfide and decrease of pH value.

结果表明，16Mn（HIC）SSCC敏感性随硫化氢浓度的增加和pH值的降低而增加。

In HAZ, crystalline particles are coarse and has high hardness and is apt to cause local corrosion, thus it is a high SSCC sensitive area.

HAZ晶粒粗大、硬度高，局部腐蚀倾向大，由此导致该区SSCC敏感性高。

Constant load tensile test was adopted to study the influence of welding material match and alloy element content on SSCC ( sulfide stress corrosion cracking) of domestic pipeline steels.

采用恒载荷拉伸法，测试了国产管线钢母材及其焊接接头的硫化物应力腐蚀开裂SSCC性能。结果表明：焊接匹配、合金元素是影响国产管线钢SSCC的重要因素。

Using the NACE standard bent-beam test, sulfide stress corrosion cracking ( SSCC) of different types microstructure in X70 grade pipeline steel with different types of microstructure was investigated.

随着国产X70管线钢在西气东输工程中的应用，国产高强度管线钢硫化物应力腐蚀开裂（SSCC）性能研究显得尤为重要。