The vanadium redox flow battery ( VRB) developed in recent years is a kind of new rechargeable battery. It is with excellent advantages, such as low cost, high security, simply technological process and power rating and energy rating being independent.

全钒氧化还原液流电池（钒电池）是日益受重视的一种新型储能电池，因其成本低、安全性高、工艺相对简单以及功率和能量相互独立等诸多特点，近来发展迅速。

A series of experimental Si-Mn series spring steel which has different vanadium content was smelt in laboratory by Fe-V or VN alloying. The penetration hardenability, temper resistance, surface decarbonization and mechanical properties of the test steel were studied.

分别采用VN、Fe-V合金在实验室冶炼了不同钒含量的Si-Mn系弹簧钢，并系统研究了其淬透性、抗回火稳定性、表面脱碳敏感性和力学性能的变化情况。

The effects of quenching temperature, cooling pattern, temper temperature and temper times on the structure and properties of high carbon and vanadium high speed steel ( HSS) roll were researched and the optimal heat treatment technical parameters were determined.

研究了淬火温度、冷却方式、回火温度和回火次数对高碳高钒高速钢轧辊组织和性能的影响，确定了最佳热处理工艺参数。

Preparation of vanadium dioxide thin film with high temperature coefficient of resistance from V_2O_5 powder by ion beam enhanced deposition

用离子束增强沉积从V2O5粉末制备高热电阻温度系数VO2薄膜

The vanadium oxide thin film has high temperature coefficient of resistance at near room temperature which is prepared by ion beam sputtering.

采用离子束溅射法制备了在室温附近具有高TCR氧化钒薄膜。

Vanadium oxide thin films are widely used in the field of uncooled IR detecting and imaging for its high temperature coefficient of resistance ( TCR).

氧化钒薄膜由于具有高电阻温度系数（TCR），近年来被广泛应用于非制冷红外探测及红外成像领域。

As the detecting material of uncooled infrared detectors, vanadium oxide ( VOX) thin films need high temperature coefficient of resistance ( TCR) and suitable film resistance for using of the device.

氧化钒薄膜作为非制冷红外探测器的热敏材料，要求具有高的电阻温度系数（TCR）与合适的电阻值，以满足器件的应用。

Bolometer performance has been improved by micromachining technology-the preparation and integration of high temperature coefficient of resistance ( TCR) VOx, nitrogen-doped vanadium oxide and gold black of high infrared absorption, respectively.

通过制备具有高电阻温度系数（TCR）的氧化钒薄膜、掺氮氧化钒薄膜和黑金吸收层并利用微加工技术手段分别将它们集成在探测器上，提高了微测辐射热计的性能。

According to the requirement of hardness on roller surface, the quenching temperature of HSS containing high carbon and high vanadium is 950~ 1100 ℃, and the tempering temperature is 530~ 550 ℃, tempering treatment one time can meet the requirement.

根据轧辊辊面硬度要求，高碳高钒高速钢的淬火温度为950～1100℃，回火温度为530～550℃，一次回火即可。

Effect of Different Vanadium Microalloying Addition on the Ratio of Tensile Strength and Yield Strength

不同钒微合金化方式对钢筋强屈比的影响

And the result of MOS capacitance test show that induced charge injection can also induce phase transition of vanadium dioxide.

通过测试结果分析发现通过感应电荷注入也可以诱导二氧化钒薄膜发生相变。

Combustion tests were conducted on a gas turbine combustion test rig, firing heavy oil admixed respectively with conventional magnesium salt vanadium inhibitor and SAYVOL-EC2 additive.

文中给出了常规镁盐抑钒剂和SAYVOL-EC2添加剂分别掺入重油在燃气轮机燃烧试验台的对比燃烧试验结果。

Removal of vanadium and sodium from heavy fuel oil

重质燃料油脱金属钒、钠技术研究

Separation and valent determination of alkali soluble vanadium in vanadium's slag treated with sodium

钠化钒渣中碱溶钒的分离与价态测定

Vanadium oxides crystallise in a layered structure and have strongly anisotropic physical properties. The unique physical and chemical properties are widely applied to the fields such as thermochromism, electrochromism, optics and electrochemistry.

钒氧化物晶体具有层状结构和很强的各向异性，它的这些特殊的物化性能使其在热致变色、电致变色、光学和电学中有着广泛的应用。

According to thermomechanical analysis in basis theoretical research, it is said that vanadium of quadrivalence and trivalence coexist in leach liquor and the influence factor of the leaching process can be worked out based on correlation kinetic equation.

由浸出基础理论研究中的热力学和动力学分析可知，浸出液中的钒是五价为主四价和三价伴存。

From the semiconductor and metal phase transition, the thermooptic effect based vanadium dioxide ( VO2) film is introduced in detail, as well as the current domestic and foreign research progress.

基于半导体和金属间的相变特性，重点介绍了基于热光效应的二氧化钒薄膜材料，描述了当前国内外的研究进展。

Factors influencing high temperature thermoplasticity of low alloy vanadium steel at temperatures ranging from 600 to 1200 ℃

600～1200℃温度范围内含钒低合金钢高温热塑性影响因素的研究

So the usage of titanium oxide reduction grade as the index of thickening in blast furnace process is reasonable, and which could represent characteristic of the blast furnace smelting iron ore bearing titanium and vanadium.

因此高炉冶炼过程中用钛氧化物还原度作为判断和控制钛渣变稠的指标能更准确地反映高炉过程特点。

Equivalent Model for Vanadium Oxide Thin Film Uncooled IR Detector

氧化钒热敏薄膜非致冷红外探测器的等效模型