shore hardness

LCR test instrument, Shore hardness test instrument and capacitive electrostrictive properties test device are used to test the effect of doped PUE.

采用LCR测试仪、邵氏硬度计和电容法电致伸缩特性测试装置研究了纳米钛酸钡掺杂对PUE的影响。

Classification and calibration method of domestic and abroad shore hardness testers

国内外邵氏硬度计的分类和校准方法探讨

Results show that the tear strength, tensile strength, elongation and Shore hardness of silicone elastomer increase in ideal value range after Parylene coating.

结果显示：Parylene涂敷后两种硅橡胶的撕裂强度、拉伸强度、扯断伸长率及邵氏硬度高于涂敷前，但数值仍在理想值范围内。

the results showed that poes had good mechanical properties. addition of carbon black had effect of reinforcing, 100% modulus, tensile strength, shore a hardness and tear strength increased drastically while impact resilience and elongation at break decreased.

结果表明，POEs具有良好的物理机械性能，加入炭黑有较好的增强作用，拉伸强度、撕裂强度、100%定伸应力和邵尔A型硬度提高，冲击弹性和扯断伸长率下降；

the results showed that the filling of short fiber evidently improved tear strength, modulus at 10% and shore a hardness of sfrc.

结果表明，短纤维的加入显著提高了SFRC的撕裂强度、10%定伸应力及邵尔A型硬度；

the tensile strength and shore a hardness of poe 8150/ caco_3 system were lower than that of poe 8003/ caco_3, and the elongation at break and impact resilience of the former were larger than that of the latter.

POE8150/CaCO3的拉伸强度、邵氏硬度比POE8003/CaCO3小，前者的拉断伸长率、冲击回弹性大于后者。

And at the same time the Shore A hardness of EPDM vulcanizate increased gradually and its tensile strength and elongation at break increased at first, and then decreased.

随着Zn（MAA）2用量的增大，EPDM硫化胶的邵尔A型硬度逐渐增大，拉伸强度和扯断伸长率都是先升高再下降。

the scale up test was carried out in a 100 t/ a plant, the product had shore a hardness 88, tensile strength 17.9 mpa, and elongation at break 1 112%.

在100t／a装置上进行了放大试验，产品的邵尔A型硬度为88度，拉伸强度为17.9MPa，扯断伸长率为1112%。

in order to improve the engineering design of rubber, the relationship between shore a hardness degrees with elastic shear modulus is built based on elastic theory.

本文从橡胶材料的性质、力学性能出发，利用弹性理论，建立了橡胶邵尔A硬度与剪切弹性模量的关系。

the tensile strength and shore a hardness increased with the increase of viscosity gravity constant.

随着填充油粘重常数的增加，SBS的拉伸强度和邵尔A型硬度增加。

the vulcanizate presented higher shore a hardness, tensile strength, modulus at 100%, modulus at 300%, and elongation at break, and lower akron abrasion loss;

硫化胶的邵尔A型硬度、拉伸强度、100%定伸应力、300%定伸应力及扯断永久变形增大，阿克隆磨耗量减小；

moreover, mechanical properties, including shore a hardness, modulus at100%, tensile strength, and tear strength of the mmt/ nbr nanocomposites were improved with the increase of amounts of starch.

随着淀粉用量的增加，该复合材料的邵尔A硬度、100%定伸应力、拉伸强度、扯断伸长率和撕裂强度均有所提高。

in general, the tensile strength and shore a hardness of pvc/ cpe/ black liquor powder composites were increased while the elongation at break was slightly decreased after thermo-oxidative aged.

添加黑液干粉的复合材料，在热氧老化后拉伸强度和邵尔A型硬度增加，断裂伸长率稍有下降。

Methods The tensile strength and Shore A hardness of samples made from HR 1 flexible gingival veneer material after being immersed in artificial saliva of 37 ℃ for 1 year and 2 years were tested.

方法测定由HR1型柔性牙龈赝复材料制备的试样在浸入人工唾液1年及2年后试样的扯断强度和邵氏A硬度的变形情况。

the results showed that the modulus at 100%, shore hardness and resistance to compression permanent set increased by adding 1.5~ 5.0 phr of maa-zn without harm to the other properties of vulcanizate.

结果表明，加入1.5～5.0份MAA－Zn，可提高硫化胶的100%定伸应力、硬度和抗压缩永久变形能力，但对其他力学性能影响甚微。

not only the shore a hardness and tensile strength of bonded rubber were maintained, but also the adhesive properties to round metal were obviously improved by adding 3 phr modified short fiber instead of 15~ 20 phr carbon black.

用3份预处理短纤维代替15~20份炭黑，不仅保持了被黏橡胶的邵尔A硬度及拉伸强度，而且明显改善了与圆形金属的黏结稳定性。

the results show that the optimum curing time is prolonged and the shore a hardness is greatly enhanced and the mechanical properties are improved by zn ( maa) 2. the heat-air aging properties and the heat-oil aging properties could still maintain high level.

结果表明，Zn（MAA）2使得ACM胶料的正硫化时间延长，硬度明显提高，力学性能得以改善，热空气老化性能以及耐热油性能仍可保持较高水平。

method of shore hardness testing for mill rolls

GB/T13313-1991轧辊肖氏硬度试验方法

Test the displacement of head-pin of Shore hardness tester by using the capacitive gate transducer, implement data collection and transfers by means of the serial communication, and realize the data analysis and process by applications of Matlab and serial communication genius program.

以容栅传感器为主实现邵氏硬度计弹簧测头的位移检测，采用串口通信方式实现了数据的传输和采集，用Matlab和串口精灵程序实现数据的分析和计算。

The Shaw Brothers Pan-Chinese Cinema; Evaluation of the Measurement Uncertainty of the Indication Error of the Shore Hardness Tester

在香港建构中国：邵氏电影的大中华视野邵氏硬度计示值误差测量结果不确定度评定

standards about shore hardness test for metallic material

有关《金属材料肖氏硬度试验方法》标准

Evaluation of the Measurement Uncertainty of the Indication Error of the Shore Hardness Tester

邵氏硬度计示值误差测量结果不确定度评定

Addition of carbon black had the effect of reinforcing, increased the 100% tensile modulus, tear strength, tensile strength and Shore A hardness, decreased the elongation at break and permanent set at break.

加入炭黑，可以起到补强作用，提高100%定伸应力、撕裂强度、拉伸强度和硬度，减小扯断伸长率和扯断永久变形。

Methods: The tensile strength, Shore A hardness and adhesive strength of the three resilient denture liner materials to PMMA were measured after being immersed in artificial saliva for one and two years.

方法：37℃人工唾液浸泡1年及2年后，测定拉伸强度、邵氏硬度及与PMMA的粘接强度。

Elongation at break 150%-250%. tension set 30%-50% and Shore hardness 85 A.

其力学性能为：拉伸强度6.57.5MPa，扯断伸长率150%250%，扯断永久变形30%50%，硬度（邵尔A型，度）85。

The results show that the polyether elastomer based on liquefied MDI and PAPI has the Shore hardness more than 65D.

结果表明，采用液化MDI或粗MDI与聚氧化丙烯醚配合使用可以制得邵D硬度大于65的聚醚型高硬度聚氨酯弹性体。

Factors affecting PVC properties, such as Shore hardness, tensile strength and medical chemical property, were discussed in detail in this article.

本文详细讨论了影响Co~（60）辐照交联聚氯乙烯邵氏硬度、拉伸强度及医用化学性能的因素。

several kinds of resin/ flexible graphite composites were prepared. the influences of the type and amount of resin on properties of composites were investigated in terms of volume density, shore hardness, specific resistance, compression ratio and rebound resilience ratio of the composite products.

采用热压法制备出不同种类树脂&柔性石墨复合材料，研究了树脂种类与用量对复合材料的体积密度、肖氏硬度、电阻率、压缩率及回弹率等性能的影响；

the cured sealant had shore a hardness 20 degree, stress at 100% 0.35 mpa and elongation at break about 900% with good workability.

密封胶硫化后的邵尔A硬度为20度、100%模量约为0.35MPa、伸长率约为900%，并具有良好的施工性能。