sorbite

After heat treatment, the microstructure of the steel is tempered sorbite.

经热处理后的试样组织均为回火索氏体。

The test results showed that Nb could prevent recrystallization of deformed lath martensite structure at 600~ 680 ℃, and the aged structure was tempered sorbite kept lath martensite phase direction with no ferrite particles discovered.

试验结果得出在600～680℃范围内，Nb能阻止变形马氏体组织的再结晶，时效组织主要为保持板条马氏体位向的回火索氏体，未发现粒状铁素体。

The 72B large gauge wire rod can obtain sorbite structure by applied micro alloying as well as controlled rolling and cooling technology The mechanisms of strength and toughness and aging phenomena of this kind of product were primarily verified

为了提高72B大规格线材的强韧性，通过微合金化及控轧控冷工艺，实现了72B大规格线材的高索氏体化，初步探明了大规格微合金化线材的强韧性机理和时效现象

The roll barrels are mainl composed of pearlitic or temper sorbite in the microstructure.

辊身金相组织为珠光体或回火索氏体.

The results showed that tempered soft zone in harden zone case produced in process of discontinuous medium frequency induction hardening which has microstructure of tempered sorbite and low hardness and low fatigue limit were major reason to cause driven gear cracking.

结果表明，因中频淬火的不连续，使淬硬层出现了回火软区，组织为回火索氏体，降低了材料的硬度和疲劳极限，最终导致从动齿轮开裂。

The typical microstructure ( Q235): the surface layer is tempered sorbite; the transition layer is pearlite and ferrite, and the partial ferrite is acicular; the core is pearlite and ferrite and the grain fineness is 8~ 10 grade.

钢筋典型的金相组织（Q235）表层为回火索氏体，过渡层为珠光体+铁素体且部分铁素体呈针状，心部为珠光体+铁素体，晶粒度8～10级；

The microstructures of heat affected zones of T91/ 10CrMo910 are tempered sorbite and thin tempered lath martensite and the toughness is good.

10CrMo910热影响区和T91热影响区的组织分别为索氏体和细的回火马氏体，韧性较好。

After high temperature tempering the microstructure transform into tempered Sorbite.

高温回火后组织为回火索氏体。

Relationship between Cyclic Strain Behavior of Tempered Sorbite in a Rail Steel and Its Dislocation Structures

回火索氏体钢轨钢循环应变行为与位错结构关系的研究

Strain-fatigue properties of pearlite and tempered sorbite in a C-Mn eutectoid rail steel have been studied by fully reversed constant total strain amplitude and plastic strain behavior in strain fatigue process has been investigated.

用全反向恒应变幅试验方法，研究了C-Mn轨钢珠光体及回火索氏体的应变疲劳行为，探讨了塑性应变在应变疲劳中的作用。

In this paper, repeated quenching and tempering processing was used to not only refine the grain size and but also keep the microstructure as tempered sorbite. Good wear resistance is also desired to be obtained by the processing.

本文设计旨在既保留回火索氏体组织又能细化晶粒的多次调质热处理工艺，以期使其耐磨性得到提高。

The technology not only guarantees that there are good microstructures of the tempered troostite and sorbite in the wire rod steel, but also makes environmental pollution and human harm decrease much.

该工艺在保证盘条钢具有良好的回火屈氏体和索氏体组织外，还减少了对环境的污染和对人体的危害。