Function and Development of Car Body Salt Spray Test

车身盐雾试验的作用与发展

La-Mo, Co-Mo and La-Co-Mo alloys were respectively deposited on titanium substrates with DSA anodes. The properties of Mo alloys were detected with methods of AES, electronic thickness gauge, micro-hardness tester, scratch adhesion test and salt spray test.

以DSA为阳极分别在钛基体上电沉积La MO、Co Mo、La Co Mo合金，采用AES、电子测厚仪、显微硬度计、划痕实验、盐雾实验等手段对镀层性能进行测试。

Corrosion resistance of CeO 2 film was evaluated by salt spray tesT.

通过盐雾试验评价了CeO2薄膜的耐蚀效果.

The corrosion resistance was explored by the methods of dropping test, neutral salt spray test.

利用点滴实验和中性盐雾实验（SST）测试了所成膜的耐蚀性能。

After 1000 hours salt spray test coating remained intact, Mechanical properties are still tough.

经过1000小时盐雾试验涂层仍保持完好，机械性能也相对较好。

It was found that the corrosion resistance ability could be consistent with the polarization curve test through 96 hours the neutral salt spray test.

并通过了96小时中性盐雾试验进行验证，发现其耐腐蚀能力和极化曲线测试结果是一致的。

This paper compares in detail the equipment, test method and function of JETTA 5 valve and 2 valve electronic spray engine control system with those of SANTANA AFE and AJR. The sameness and differences of different brands and types are sought.

对捷达5气门与2气门电喷发动机控制系统以及桑塔纳AFE与AJR电喷发动机控制系统的配置、检测方法和功能作了详细对比，并寻求其不同品牌、不同年代产品间的相同点与差异点。

The antirust performance was tested using salt spray test after drying.

烘干后采用盐雾试验进行测定其防锈的性能。

Chemical property testing: salt spray test of materials, corrosion test of stainless steel.

化学性能测试: 材料的盐雾试验 、 不锈钢腐蚀试验等.

Simulated test in lab and industrial test in mine have proved its spray and dust-settling effect.

通过实验室模拟试验和现场工业性试验验证了掘进高效喷雾降尘系统的雾化效果和降尘效率.

Through the process test 、 wearing test and microstructure observation and analysis, the convention performance of oxygen-acetylene flame spray welded layer is studied.

通过工艺试验、耐磨试验和显微组织观察分析，研究了氧-乙炔火焰喷焊层的常规性能。

Comparative Analysis of Salt Spray Test Standards ISO 9227:2006 and ISO 9227:1990

盐雾试验标准ISO9227：2006与ISO9227：1990对比分析

No spot corrosion occurs on the surface of the sample with titanate conversion coating after 336 h of salt spray test.

钛酸盐转化处理的样品经336h盐雾试验表面无点腐蚀发生。

Corrosion resistance of aluminum-tube surface with silane-rare earth composite coating was studied respectively by electrochemical means, dropping corrosion and salt spray test.

采用电化学、点滴和盐雾实验对铝管表面硅烷稀土复合膜的耐蚀性进行考察。

Discussions and Analysis on Bubbling Around Crosscut of Film in Neutral Salt Spray Test

中性盐雾试验中漆膜划痕处起泡探析

Corrosion The corrosive degree of specimen in neutral salt spray test for 200h was the same as one in coal mine water for a year.

200h中性盐雾试验相当于煤矿水质一年的腐蚀量。

The results show that white sealing film can be obtained, and no white rust observed after 48 hours neutral salt spray test.

结果表明：采用该工艺能得到白色封闭膜，中性盐雾试验48h后不出现白锈。

The iridescent passivation film is also tested by Tafel curve test, impedance measurement and corrosion current test and neutral salt spray test.

并对彩色钝化膜进行了Tafel曲线测试、阻抗测试、腐蚀电流试验和中性盐雾试验。

The influences of heat treatments on anti-corrosion properties of some stainless steels are evaluated through salt spray test.

通过盐雾试验评价了热处理工艺对不锈钢腐蚀特征的影响。

The corrosion resistance of Zn-Ni-P alloy was superior to Zn-Ni alloy by salt spray test.

盐雾腐蚀试验结果表明，Zn Ni P合金较Zn Ni合金耐蚀性大大提高。

Study on Process and Corrosion Resistance of Ni-P Alloy Brush Plating layers in Salt Spray Test

电刷镀Ni-P合金工艺及其耐盐雾腐蚀性能研究

Corrosion resistance of an entire-bright nickel-phosphorus alloy coating was studied by means of salt spray test, immersion test and anodic polarization etc.

采用个性盐雾实验、浸泡实验和阳极极化曲线测试了全光亮镍磷合金镀层耐蚀性。

Study on Neutral Salt Spray Test of Super High-Build Epoxy Heavy Duty Coatings

超厚膜环氧重防腐涂料的耐中性盐雾性能研究

The result of salt spray test was the same as that of the pure gold deposit.

耐盐雾腐蚀与纯金相同。

This paper has briefly described two national standards for salt spray test and added necessary explanation for correct implement of them.

简要介绍了盐雾试验的两项国家标准，对标准的正确应用作了必要的说明。

Salt Spray Test Standard and Its Implement

盐雾试验标准及其实施

Discussion on the Mechanism and Method of Salt Spray Test in Gold plated Layer

镀金层盐雾试验机理及方法探讨

This article chooses suitable paints, and carried out the adhesion and salt spray test against the coating.

本文选择了相关涂料，并对涂层进行了盐雾和附着力试验。

Approach to Salt Spray Test and Their Result Evaluation

有关涂料盐雾试验及结果评价的探讨

The results of salt spray test and contact corrosion test further approved the same conclusion.

从盐雾试验和接触腐蚀试验结果进一步证实这一结论：注入试样比非注入试样在抗蚀性方面提高很大。