steel wheel

Modern Technology Development of Passenger Car Steel Wheel

现代乘用车钢制车轮的技术发展

Numerical simulation of new ring rolling process of tubeless steel wheel

无内胎钢制车轮辗环成形新工艺及其数值模拟

The effect of flaking on mechanical properties of wheel steel was investigated.

研究了车轮钢中白点对力学性能的影响.

The semi-artificial thermocouple is composed of the steel substrate and a single Ni-Cr thermocouple wire which is embedding in diamond grinding wheel.

该装置在金刚石磨轮上布设单根镍铬电偶丝，同磨轮基体组成半人工热电偶。

The mechanism of flaking in wheel steel and the effects of flaking on fracture were investigated.

研究了车轮钢中白点形成的机理以及白点对断口形貌的影响.

The aluminum alloy wheel will replace the steel wheel gradually because of it's many excellences.

铝合金车轮以其诸多优点将会逐渐代替钢制车轮.

Probe into thermal fatigue fracture behaviour of certain cast steel wheel material under thermal cycling of 600 ℃~ 20 ℃

铸钢车轮材料在600℃~20℃循环温度幅下热疲劳断裂行为探讨

The fore on the grinding wheel loading mechanism of steel conditioning machine tool is analyzed theoretically.

对钢坯修磨机砂轮加载机构进行了受力分析。

Damage behavior of wheel cast steel was analyzed under thermal fatigue test at 450 ℃~ 20 ℃.

研究了一种铸钢车轮材料在450℃~20℃热循环下破坏行为。

Analysis on Entrapped Slag Defect of Cast Steel Wheel Poured Continuously by Bottom Pouring Ladle

用底注包连续浇注铸钢车轮产生夹渣缺陷的分析

The thermal fatigue fracture characteristics of a cast steel for wheel in different temperature cycles from 750 ℃ to 20 ℃ have been studied by using SEM.

分析一种车轮铸钢材料在750℃和20℃之间不同温度循环范围的热疲劳断口形貌特征。

The thermal fatigue fracture behavior of some cast steel wheel material under thermal cycling of 600~ 20 ℃ was studied.

研究了铸钢车轮材料在循环温度幅600~20℃下的热疲劳断裂行为。

The fracture behavior of Fe-based and Ni-based thermally sprayed coatings on wheel cast steel has been investigated under the thermal fatigue test at 450 ℃-20 ℃.

分析了某铸钢车轮试样热喷涂层热疲劳试验断口特征。在铸钢车轮材料表面分别热喷涂铁基和镍基两种合金涂层，进行450℃-20℃下热疲劳试验，对断口形貌进行观察。

When the mandrel speed is too high or too low or spinning wheel speed is too large, variable cross-section tubeless steel wheel rim formed parts will have the defects.

当芯模转速过高或过低，旋压轮转速过大时，变截面无内胎钢车轮轮辋成形件将有上述缺陷产生。

Steel wheel is used as a tool for cranes.

铸钢手轮是用于起重机的一种工具.

Robust design with cast iron body. nodular iron worm wheel adn carbon steel worm.

铸铁的外壳, 球墨铸铁的蜗轮,碳钢的蜗杆,设计结构坚固.