curing time的例句大全

In order to use shrub materials to produce wood based panels reasonably, pH value, buffering capacity and curing time of 6 main shrub species in the north western China were measured.

为了合理开发我国西北地区的沙生灌木，研究了内蒙西部地区沙柳、柠条、沙棘、红柳、桦棒、杨柴6种主要沙生灌木的pH值、酸碱缓冲容量与UF胶混合物固化时间。

the results show that boron phenolic resin can obviously improve ablative properties of material, but it has inverse effect on tensile strength and elongation-to-break of materials and prolongs curing time of matrix material.

结果表明，硼酚醛树脂可以显著提高烧蚀材料的耐烧蚀性能，同时对材料的拉伸强度和断裂伸长率有相反的影响，并对胶料具有延迟硫化作用。

An Experiment Study on the Influence of Air Content and Curing Time on Concrete Anti-Chloride Permeability Performance

含气量和养护龄期对混凝土抗氯离子渗透性能影响的试验研究

As to this type of lightweight soil, direct shear test is used to study the influencing factors of cement content, EPS beads content and curing time on the shear parameters.

通过直接剪切试验，获取了淤泥EPS颗粒混合轻质土的抗剪强度参数，即粘聚力与内摩擦角。

It can be quicky cured and resisted high temperature for class H in a short curing time and low evaporation losses.

它耐高温达到H级，固化速度快，贮存周期长，挥发率低。

influence of curing time on structure and properties of sbr ebonite

硫化时间对硬质SBR结构与性能的影响

Low temperature and high vacuum tumble technology being widely used at home and abroad can shorten the curing time and improve product textural properties.

低温真空滚揉能缩短腌制时间，改善产品质构，目前国内外广泛采用；

And as the curing time extended, the hardness, tensile strength and elastic modulus of SBR ebonite increased and its T_g rose significantly.

随着硫化时间的延长，硬质SBR的硬度、拉伸强度及弹性模量增大，玻璃化温度显著提高。

This paper studies the effect of curing time and filling on mechanical property of mouse pad.

研究了硫化时间、补强剂对鼠标垫力学性能的影响。

Test and Study of Influence of Curing Time on Features of a Lime-flyash Soil Project

养护龄期对二灰土工程特性的影响试验研究

Laboratory experiment is carried out on the mechanical property of CFG pile material ( fly ash concrete) composed of a large quantity of ⅲ a-fly ash mixture. The relationships between compressive strength and the proportion of fly ash substituting cement, and curing time are studied.

通过材料实验，对大掺量Ⅲa级粉煤灰素混凝土构成的CFG桩桩身材料进行力学性能方面的试验研究，主要探讨抗压强度与材料配比、龄期之间的关系。

With the increase of curing time, the strength of hardened cement increases continually in the later of the reaction period.

随养护时间增长，混合材料后期强度持续增加。

The selection of process conditions such as the dosage of binder SX in pigment printing, curing temperation and curing time was discussed.

探讨了粘合剂SX在印花工艺中用量、焙烘温度、焙烘时间等条件的选择。

studies on the relationship between castanopsis hystrix wood properties and curing time of uf

红锥木材性质与UF胶固化时间关系的研究

Influencing of curing time on film hardness is discussed through modifying the ratio of paint and curing agent. The defects from spraying process and the countermeasures are narrated.

通过调整漆与固化剂比例，讨论了固化时间对漆膜硬度的影响，同时论述了喷涂过程中产生的缺陷和采取的措施。

Epoxy resin grouts have low viscosity, good grouting property and the coagulation or curing time of their serosity can be regulated according to the demand.

环氧树脂化学灌浆材料由于其灌浆材料粘度小，可灌性好；浆液的胶凝或固化时间可以按需要进行调节；

The strength of filling body, filling mortar weight concentration and curing time are in direct proportion relationship.

且充填体的强度与充填砂浆重量浓度、养护时间之间均成正比例增加关系，没有出现异常情况。

Come through the curing temperature by differential scanning calorimetry ( DSC), Curing trial in combination with curing reaction appropriate curing time.

通过差式扫描量热法（DSC）得出固化温度，并结合固化试验得出固化反应适宜的固化时间。

Experimental results show that with crisscross winding method and 30% to 40% of resin content and 150 N to 200 N of winding tension for a fiber strand and GPC chart analysis to determine curing time, better comprehensive performance of the composite materials can be obtained.

结果表明：采用交替铺层方式缠绕成型，含胶量控制在30%～40%（质量分数），缠绕张力控制在150N～200N，采用GPC谱图控制固化时机，得到的复合材料综合性能较好；

The effect of binder and curing time to the pebble jellied meat

增稠剂与腌制时间对水晶肉冻的影响