curing time的例句大全

Take the average temperature in the curing time as curing temperature.

养护温度取各湿喷桩养护期的平均气温。

The compressive strength also varied with the curing time.

养护时间不同，其抗压强度有明显的差异。

Experimental Study of Influencing Factors of Cement Curing Time

水泥候凝时间及其影响因素的试验研究

Study on tye Decrease of Autoclave Curing Time for Aerated Pfa Concrete

缩短粉煤灰加气混凝土蒸压养护时间的研究

In this paper application of "static placing in heated room" has been proposed as a means for decreasing the autoclave curing time of aerated pfa concrete.

本文提出了采用热室静停作为缩短粉煤灰加气混凝土蒸压养护时间的手段。

The optimize curing time under different temperatures was also investigated.

另外，对不同养护温度下土壤聚合反应的最佳养护时间也进行了研究。

The results showed that the curing time of product extended when the heat diffusivity decreased;

结果表明，热扩散系数降低时制品的硫化时间延长；

Low temperature and high vacuum tumble technology being widely used at home and abroad can shorten the curing time and improve product textural properties.

低温真空滚揉能缩短腌制时间，改善产品质构，目前国内外广泛采用；

Influencing of curing time on film hardness is discussed through modifying the ratio of paint and curing agent. The defects from spraying process and the countermeasures are narrated.

通过调整漆与固化剂比例，讨论了固化时间对漆膜硬度的影响，同时论述了喷涂过程中产生的缺陷和采取的措施。

And as the curing time extended, the hardness, tensile strength and elastic modulus of SBR ebonite increased and its T_g rose significantly.

随着硫化时间的延长，硬质SBR的硬度、拉伸强度及弹性模量增大，玻璃化温度显著提高。

Laboratory experiment is carried out on the mechanical property of CFG pile material ( fly ash concrete) composed of a large quantity of ⅲ a-fly ash mixture. The relationships between compressive strength and the proportion of fly ash substituting cement, and curing time are studied.

通过材料实验，对大掺量Ⅲa级粉煤灰素混凝土构成的CFG桩桩身材料进行力学性能方面的试验研究，主要探讨抗压强度与材料配比、龄期之间的关系。

With the increase of curing time, the strength of hardened cement increases continually in the later of the reaction period.

随养护时间增长，混合材料后期强度持续增加。

The selection of process conditions such as the dosage of binder SX in pigment printing, curing temperation and curing time was discussed.

探讨了粘合剂SX在印花工艺中用量、焙烘温度、焙烘时间等条件的选择。

Epoxy resin grouts have low viscosity, good grouting property and the coagulation or curing time of their serosity can be regulated according to the demand.

环氧树脂化学灌浆材料由于其灌浆材料粘度小，可灌性好；浆液的胶凝或固化时间可以按需要进行调节；

The curing reaction of hydrogenated terpinene maleic anhydride ( HTMA) with bisphenol A epoxy resin was investigated by FT-IR spectrum, and the curing degree, gelation time and its affecting factors were analyzed.

采用FT-IR光谱研究了氢化萜烯马来酸酐（HTMA）与双酚A型环氧树脂的固化反应过程，并分析了固化度、凝胶时间及其主要影响因素。

The test results show that the longer the time of moist curing, the higher the values of compressive strength, splitting tensile strength, elastic modulus and critical stress intensity factor.

试验结果表明，抗压强度、弹性模量、抗拉强度以及临界应力强度因子随标准养护时间的增长而增大，弹性模量对养护条件的敏感性最大。

Determination of Curing Temperature and EV Time for Thick walled Rubber Article

橡胶厚制品硫化温度与等效硫化时间的测定

The paper used FTIR to monitor the curing progress and studied the effects of photoinitiators on the relationship of exposure time and conversion.

用FTIR跟踪监测环氧丙烯酸酯胶粘剂光固化过程并研究了光引发剂体系中辐射时间与双键转化率的关系。

The activity of curing reaction of modified rosin based alicyclic epoxy resin with modified methyl hexahydrophthalic anhydride was investigated by thermal analysis and gelatin time determination.

采用热分析及凝胶时间测定方法研究了以松香为基础的改性脂环基环氧树脂与改性甲基六氢苯酐的固化反应活性；

While little sulfur was added to the curing system of DTDM, the mixture cured faster, had shorter pre vulcanization time and worse properties.

当少量硫黄与DTDM并用时，胶料的硫化速度加快、焦烧时间缩短，但对力学性能有所损害；