The tear strength and abrasion resistance of NR/ SBR vulcanizates were improved by joining the reinforcing resin AD-1600, reinforcing resin OD-60 and 10 phr TPI.

通过加入补强树脂AD-1600、补强树脂OD-60和10份TPI均可提高NR/SBR硫化胶的撕裂强度、耐磨耗性。

The HDPE composite materials show the behaviors of brittle tensile break when the dosage of filler is over 70 phr.

当超细Mg（OH）2填料用量达到70份时，HDPE复合材料表现出明显的脆性拉伸断裂行为。

By adding 12 phr decabromodiphenyl oxide ( DBDPO)/ Sb_2O_3 flame retardance system, the flame retardance property of glass fibre reinforced PET could reached the grade of UL 94 V-0.

添加12份十溴二苯醚/Sb2O3复合阻燃剂，可使玻纤增强PET的阻燃性能达到UL94V-0级。

The EPDM/ PA thermoplastic elastomer with PA 35 phr had good mechanical properties, resistance to solvent and thermal ageing properties.

PA用量为35份的EPDM/PA热塑性弹性体具有良好的力学性能、耐溶剂性能和耐热老化性能；

When EVA content is within 10 phr, the PE insulant's MFR, dielectric strength, thermal extensibility, elongation at break, volume resistivity and crosslinkage can meet the technical requirements.

EVA的添加量在10phr之内，绝缘料的MFR、介电强度、热延伸性能、断裂伸长率、体积电阻率、交联度满足技术指标要求；

A new inner ply compound with high SR proportion and low polymer content was developed by increasing the blending ratio of SR from 30% to 40%, changing the type of carbon black and adding 5 phr of silica.

将内层胶配方中合成橡胶用量由原来的30份提高到40份，通过改变炭黑的品种、添加5份白炭黑等方法降低原生产配方的含胶率。

Use black/ silica reinforcing system and Si69/ sulfur/ sulferamide ( 1/ 1/ 1) curing system in tread compound and increase the NR proportion from 80 phr to 90 phr in shoulder compound for formulation;

配方设计方面包括胎冠胶采用炭黑/白炭黑补强体系，Si69、硫黄及次磺酰胺类促进剂的用量比为1/1/1，胎肩胶中NR用量由80份增大为90份等；

the micromorphology, mechanical properties, resistance to aging and thermal stability of nr/ m-ccr composites were improved markedly. the comprehensive properties were the best when the m-ccr was less than 10 phr.

NR/M-CCR复合材料的力学性能、耐老化性能和热稳定性能显著提高，且当M-CCR用量少于10份时，NR/M-CCR复合材料的综合性能最佳。

NBR. EPDM. SBR , the ρ v of the vulcanizate with 70 phr was between 0 . 9~1.3Ω.

另外,将HG- S以 70phr填充天然橡胶、丁苯橡胶 、 丁腈橡胶、乙丙橡胶时,硫化胶的体积电阻率在0.9～1.3Ω·cm之间.

The maximum tensile strength retension and elongation ultimate retension of EPDM vulcanizate after aging were obtained by adding 0.5 phr of TMPTA;

当TMPTA用量为0.5份时，EPDM硫化胶的拉伸强度保持率和扯断伸长率保持率达到最大值；

FKM/ MVQ blends show superior mechanical properties when DCP content is 1 phr.

当DCP用量为1份时，共混胶的力学性能良好。

The results showed that TPI thermal deformation temperature decreased with increasing sulfur content. The content of sulfur should be less than 2.5 phr in the shape memory materials.

结果表明，TPI硫化胶的形变热刺激温度随硫黄用量的增加而降低，在形状记忆材料中，硫黄用量不应大于25份；

With names like Google and Microsoft announcing PHR offerings over the web, data portability and availability will start hitting home with many more people than just those on social networking sites.

比如Google和微软都宣布提供基于Web个人健康档案的服务，那么可以预见的是数据可移植性和有效性将会叩开更多普通人的家庭，而不仅仅局限于社会网络站点。

The result of MFR showed that the compounded fire-retardant with 40 phr could meet the needs of processing craftwork.

熔体流动速率（MFR）的测定表明当复合阻燃剂的添加量为40份时，仍能满足加工工艺的要求。

as the level of activating agent was 1 phr , the effectiveness was best.

活化剂用量为1质量份时，活化效果最好。

aim: in this work, we investigated the difference of membrane capacitance, membrane current, current density and i-v curves between smooth muscle cells isolated from pulmonary hypertension rat ( phr) or normotensive rat ( ntr) pulmonary arteries.

目的：观察肺动脉高压大鼠（PHR）肺动脉平滑肌细胞膜电容（Cm）、膜电流（I）、电流密度（pA/pF）及I-V曲线，并与正常SD大鼠进行比较。

the results showed that the modulus at 100%, shore hardness and resistance to compression permanent set increased by adding 1.5~ 5.0 phr of maa-zn without harm to the other properties of vulcanizate.

结果表明，加入1.5～5.0份MAA－Zn，可提高硫化胶的100%定伸应力、硬度和抗压缩永久变形能力，但对其他力学性能影响甚微。

setting the phr liner hanger

悬挂器座挂

not only the shore a hardness and tensile strength of bonded rubber were maintained, but also the adhesive properties to round metal were obviously improved by adding 3 phr modified short fiber instead of 15~ 20 phr carbon black.

用3份预处理短纤维代替15~20份炭黑，不仅保持了被黏橡胶的邵尔A硬度及拉伸强度，而且明显改善了与圆形金属的黏结稳定性。

(phr v) dress sb down scold sb; tell sb off

训斥，斥退（某人）。