phr

However, after the dosage of Talc exceeded 10 phr, the elongation at break of blends reduced dramatically.

但是, 当Talc用量超过10份后, 体系的拉伸断裂伸长率明显下降.

NBR. EPDM. SBR , the ρ v of the vulcanizate with 70 phr was between 0 . 9~1.3Ω.

另外,将HG- S以 70phr填充天然橡胶、丁苯橡胶 、 丁腈橡胶、乙丙橡胶时,硫化胶的体积电阻率在0.9～1.3Ω·cm之间.

The HDPE composite materials show the behaviors of brittle tensile break when the dosage of filler is over 70 phr.

当超细Mg（OH）2填料用量达到70份时，HDPE复合材料表现出明显的脆性拉伸断裂行为。

The results showed that the vulcanizate had best mechanical properties while 3% GMA in copolymer and 1.5 phr ammonium benzoate in vulcanization recipe.

结果表明，共聚单体中甲基丙烯酸缩水甘油酯用量为2%～3%，苯甲酸铵用量为1.5份时，硫化胶的力学性能最好。

All along or ( informal ) right along adv. phr.

自始至终;一直就;从开始便.

With names like Google and Microsoft announcing PHR offerings over the web, data portability and availability will start hitting home with many more people than just those on social networking sites.

比如Google和微软都宣布提供基于Web个人健康档案的服务，那么可以预见的是数据可移植性和有效性将会叩开更多普通人的家庭，而不仅仅局限于社会网络站点。

The EPDM/ PA thermoplastic elastomer with PA 35 phr had good mechanical properties, resistance to solvent and thermal ageing properties.

PA用量为35份的EPDM/PA热塑性弹性体具有良好的力学性能、耐溶剂性能和耐热老化性能；

As the level of activating agent was 1 phr the effectiveness was best.

活化剂用量为1质量份时,活化效果最好.

Calcined clay/ LEE white slippery powder/ PY ⅱ water white mica powder/ titanium white powder 105~ 115 phr;

补强填充剂为煅烧陶土、LEE白滑粉、PY－Ⅱ型水白云母粉和钛白粉并用体系（105～115份）；

The heat diffusivity of the compound, in which the addition level of carbon black was in the range of 25~ 40 phr, increased by 5% as the addition level of carbon black increased by every 1 phr.

而胶料中炭黑用量在25～40份范围内时，炭黑用量每增大1份，则胶料的热扩散系数增大约5%。

The results showed that TPI thermal deformation temperature decreased with increasing sulfur content. The content of sulfur should be less than 2.5 phr in the shape memory materials.

结果表明，TPI硫化胶的形变热刺激温度随硫黄用量的增加而降低，在形状记忆材料中，硫黄用量不应大于25份；

The tear strength and abrasion resistance of NR/ SBR vulcanizates were improved by joining the reinforcing resin AD-1600, reinforcing resin OD-60 and 10 phr TPI.

通过加入补强树脂AD-1600、补强树脂OD-60和10份TPI均可提高NR/SBR硫化胶的撕裂强度、耐磨耗性。

FKM/ MVQ blends show superior mechanical properties when DCP content is 1 phr.

当DCP用量为1份时，共混胶的力学性能良好。

The result of MFR showed that the compounded fire-retardant with 40 phr could meet the needs of processing craftwork.

熔体流动速率（MFR）的测定表明当复合阻燃剂的添加量为40份时，仍能满足加工工艺的要求。

By adding 12 phr decabromodiphenyl oxide ( DBDPO)/ Sb_2O_3 flame retardance system, the flame retardance property of glass fibre reinforced PET could reached the grade of UL 94 V-0.

添加12份十溴二苯醚/Sb2O3复合阻燃剂，可使玻纤增强PET的阻燃性能达到UL94V-0级。

A new inner ply compound with high SR proportion and low polymer content was developed by increasing the blending ratio of SR from 30% to 40%, changing the type of carbon black and adding 5 phr of silica.

将内层胶配方中合成橡胶用量由原来的30份提高到40份，通过改变炭黑的品种、添加5份白炭黑等方法降低原生产配方的含胶率。

The maximum tensile strength retension and elongation ultimate retension of EPDM vulcanizate after aging were obtained by adding 0.5 phr of TMPTA;

当TMPTA用量为0.5份时，EPDM硫化胶的拉伸强度保持率和扯断伸长率保持率达到最大值；

As a result, they apply a + 15 bonus to their Physical Resistance ( PhR ) .

因此, 他们另外加 15点 在他们物理抵抗.

Use black/ silica reinforcing system and Si69/ sulfur/ sulferamide ( 1/ 1/ 1) curing system in tread compound and increase the NR proportion from 80 phr to 90 phr in shoulder compound for formulation;

配方设计方面包括胎冠胶采用炭黑/白炭黑补强体系，Si69、硫黄及次磺酰胺类促进剂的用量比为1/1/1，胎肩胶中NR用量由80份增大为90份等；

When EVA content is within 10 phr, the PE insulant's MFR, dielectric strength, thermal extensibility, elongation at break, volume resistivity and crosslinkage can meet the technical requirements.

EVA的添加量在10phr之内，绝缘料的MFR、介电强度、热延伸性能、断裂伸长率、体积电阻率、交联度满足技术指标要求；

The optimal concentrations of DCP, VTES and DBTL obtained from the orthogonal designing, were 0.10 PHR, 2.5 PHR and 0.15 PHR, respectively.

正交实验获得DCP、VTES及DBTL的最佳用量分别为0.10份、2.5份、0.15份；