When resin content was 4%, the wheat-straw particleboard of 0. 6g/ cm3 could fully meet requirement;

当施胶量为4%时，密度为0.6g／cm3的麦秸刨花板的力学性能完全满足国家标准要求；

Books and periodicals on the cohesion and effectiveness of resin content, gummed coating thickness and grooving.

书刊的黏结效果与上胶量 、 背胶的涂布厚度及开槽大小有关.

The Resin Content on-line Monitoring in Composite Prepreg Tapes Using Beta-ray Technique

用β射线技术在线监测复合材料预浸带树脂含量

Increasing the temperature of preheating, the mandrel-pressure roller and the hot air gun and choosing the moderate pressure of pressure roller come along with a rise in interlaminar shear strength ( ILSS) and a reduction in resin content.

结果表明：提高芯模压力辊温度、热风枪温度、预热器温度，选择适中的压力辊压力，在层间剪切强度提高的同时，树脂含量下降。

the ablative mechanism of boron phenolic resin/ nbr ablative material system was discussed, and the effects of boron phenolic resin content on ablative, mechanical and processing properties of the ablative materials were investigated in detail.

探讨了硼酚醛树脂/丁腈胶烧蚀材料体系的烧蚀机理，并详细研究了硼酚醛树脂含量对烧蚀材料烧蚀性能、力学性能和加工性能的影响。

Single face corrugated machine speed slow increases Corrugating cord to peak cohniiand resin content.

单面瓦楞机车速过慢,会增大瓦楞楞峰的着胶量.

Continuous monitoring of resin content in carbon/ phenolic prepreg cloth by β-ray method

炭/酚醛预浸布树脂含量的β-射线连续监测

Calculation of Bleeding System in Composite Autoclave Forming and Selection of Prepreg Resin Content

热压罐法复合材料成形吸胶系统的计算及预浸料树脂含量的选择

Glued resin content affected longitudinal tensile strength significantly and the impacting of board density to all mechanical properties reached to a significant level. In the testing range other factors and levels affected the board properties indistinctively.

单板涂胶量对板材顺纹抗拉强度影响达到显著水平，板材密度对各力学性能影响均达到显著水平；其余因素各水平在试验选定范围内，并未对板材各性能指标有显著的影响。

However, to the acacia flakeboard with the same density, whether the resin content is high or not, the pressure of the central layer of mat is fluctuating, but always keeps it in the horizontal direction, the 3 pressing phase is not emerged.

同样密度的刺槐刨花板，不论施胶量大小，板坯芯层压力波动大，但几乎保持水平方向，没有出现三段压力之分。

Experimental results show that with crisscross winding method and 30% to 40% of resin content and 150 N to 200 N of winding tension for a fiber strand and GPC chart analysis to determine curing time, better comprehensive performance of the composite materials can be obtained.

结果表明：采用交替铺层方式缠绕成型，含胶量控制在30%～40%（质量分数），缠绕张力控制在150N～200N，采用GPC谱图控制固化时机，得到的复合材料综合性能较好；

resin content is too big, since some glue will result in high volume water absorption in the paper.

胶量太大，因为胶水量大必然使纸张吸收水分大。

with further increasing the epoxy resin content, the flexural modulus and tensile strength increase slowly and the impact strength varies slightly, while the elongation at break decreases rapidly.

继续增加环氧树脂的含量，共混物的拉伸强度和弯曲模量增加缓慢，冲击强度无明显变化，断裂伸长率进一步降低。

in this paper the preliminary study was made on the effect of the press temperature, water content of wood particle and resin content with the properties of composite made from recycled polypropylene plastic and wood particle.

另外本文还采用单因素试验方法初步研究了刨花含水率、热压温度和施胶量等工艺参数对异氰酸酯胶木材-回收聚丙烯废塑料复合刨花板的影响规律。

Study on the optimal resin content of high strength bulletproof glass fiber reinforced plastics

防弹用纤维复合材料最佳树脂含量研究

The crystallinity reach its peak when the content of epoxy is 1%, with the increase of epoxy resin content, the crystallinity of nylon 11 alloy decreases.

环氧树脂用量为1%时，尼龙11共混合金体系的结晶度最大，此后随着环氧树脂的加入，尼龙11结晶度随之降低。

The resin content put little influence on the temperature changes in central layer of the acacia flakeboard.

施胶量对刺槐刨花板芯层温度影响非常小。

The development of a sort of high strength coated sand with low resin content;

高强度低树脂量覆膜砂的研制；

The influence of the resin content on temperature and pressure in the hot-pressing process of flakeboard is illustrated for first time based on the experiment results: ( 1) consuming adhesive is favorable to the heat transfer process on the direction of thickness.

首次通过实验阐明了施胶量对刨花板热压过程中温度和压力的影响：（1）施加胶粘剂有利于板坯厚度方向上的传热。

Research of Analysis Method for Fluorocarbon Resin Content in Fluorocarbon Lacquer

氟碳漆中氟碳树脂含量的分析方法研究