sintered density的例句大全

However, as it increases to a high value(η 0.30 kJ/ mm3), the sintered density shows a decrease.

但若增至过高（大于0.30kJ/mm3），烧结致密度则呈下降趋势。

The sintered density increases sharply with increasing the energy density by volume to a critical value(η about 0.15 kJ/ mm3).

当能量体密度增至一临界值（约0.15kJ/mm3）时，烧结致密度有显著提高；

The microstructure evolution of sintered HAP was studied under different laser energy density.

揭示了不同激光能量密度下烧结样微结构的变化规律。

Ceramics were sintered at 950 ℃ by adding ZnO as sintering assistant in CZP powder, and the relative density, average thermal expansion coefficients, strength resistance, and microstructure of the ceramics were measured and observed.

添加ZnO为烧结助剂，将CZP粉体在950℃下烧结成陶瓷，测定和观察所制备陶瓷的相对密度、平均热膨胀系数、抗压强度和显微结构。

improving compaction pressure can increase the density and vickers hardness of sintered ceramics.

随着粉料成型压力的升高，烧结后瓷体的密度及维氏硬度均增大；

After re-pressing, annealing and re-sintering, difference between Hc values of sintered strips with various density diminishes.

不同密度的烧结带材经过复压 、 退火、复烧后, 带材的Hc值差距缩小.

The relationship between the density ratio of sintered bodies and temperature was investigated by SEM and Archimedean method.

研究了在氨压条件下温度对烧结致密度的影响。

How the fineness of powdered magnesia due to grinding, briquetting pressure and light roasting temperature affect the bulk density of sintered magnesia were investigated through tests.

考察了细磨程度、成形压力及轻烧温度对烧结镁砂密度的影响。

The density of tungsten heavy alloy plates liquid phase sintered in continuing furnace was investigated with drainage, and its distributions both in width and length were studied.

采用阿基米德排水法，测量了连续液相烧结钨基高比重合金板的密度，并对其在长度和宽度方向上的密度分布进行了研究。

the influence of various bronze powder additions on density aisi 316 l sintered stainless steel was studied.

结果表明:添加青铜粉末提高了316L不锈钢的生坯密度.

The density of sintered pellets increases with the sintering temperature at constant sintering time and the increment of the sintered-pellet density with the sintering temperature is much more significant than that with sintering time.

在相同的烧结时间内，提高烧结温度，烧结块的密度随之提高，且提高程度比延长烧结时间提高的程度更为显著。