sintered density

The density of sintered pellets increases with the sintering temperature at constant sintering time and the increment of the sintered-pellet density with the sintering temperature is much more significant than that with sintering time.

在相同的烧结时间内，提高烧结温度，烧结块的密度随之提高，且提高程度比延长烧结时间提高的程度更为显著。

The relationship between the density ratio of sintered bodies and temperature was investigated by SEM and Archimedean method.

研究了在氨压条件下温度对烧结致密度的影响。

After re-pressing, annealing and re-sintering, difference between Hc values of sintered strips with various density diminishes.

不同密度的烧结带材经过复压 、 退火、复烧后, 带材的Hc值差距缩小.

However, as it increases to a high value(η 0.30 kJ/ mm3), the sintered density shows a decrease.

但若增至过高（大于0.30kJ/mm3），烧结致密度则呈下降趋势。

How the fineness of powdered magnesia due to grinding, briquetting pressure and light roasting temperature affect the bulk density of sintered magnesia were investigated through tests.

考察了细磨程度、成形压力及轻烧温度对烧结镁砂密度的影响。

The sintered density increases sharply with increasing the energy density by volume to a critical value(η about 0.15 kJ/ mm3).

当能量体密度增至一临界值（约0.15kJ/mm3）时，烧结致密度有显著提高；