resistance electrode

GBL was added to promote the formation of the negative electrode surface of the low resistance film, reducing the polarization of the battery, the conductivity of the film was increased.

加入GBL促进负极表面低阻抗膜的形成，降低电池的极化，增大膜的导电性。

The results show that electrode degradation mechanism was basically caused by wear due to fracture of local welding between the electrode tip surface and zinc coated sheet steel happen at electrode surface and alloying between electrode and zinc on zinc coated steel during resistance spot welding zinc coated steel.

结果表明：点焊镀锌钢板时电极的失效机制主要是电极和镀锌板之间局部焊接的断裂发生在电极表面而导致的电极磨损以及电极和镀锌板表面的锌之间的合金化。

Design of Interruption Driver of Non-resistance Pulse Generator for Wire-electrode Cutting

线切割无阻脉冲电源中断驱动程序设计

Plate electrode of ZC 36 type high resistance meter is put into thermo tank. The insulation resistance of dust is measured with high resistance low voltage, and then the specific resistance is calculated.

应用ZC-36型高阻计测量箱中的圆盘电极改装入恒温箱中，采用高阻计低压法测量出粉尘的绝缘电阻R，再经计算得出粉尘的比电阻ρ。

A homogenous and dense film of PAn coating electrode of stainless steels has better corrosion resistance.

只有均匀、致密的聚苯胺膜才有较好的耐蚀能力.

The effect of TiC coating in electrode tip surface on spheriform electrode degradation during resistance spot welding zinc coated steel was investigated by SEM, EDX and XRD.

利用SEM、EDX和XRD等方法分析了在点焊镀锌钢板时球形电极表面熔敷TiC涂层对电极失效的影响。

The instrument is specially designed for simplicity in measuring the contact resistance of switch, relay, plug, connector, or between electrolytic lead leg and electrode.

该仪器是专为简单的测量开关接触电阻，继电器，插头，连接器，或腿之间的电解铅和电极。

The electrochemical reaction resistance can be decreased adopting wet method, the reactive resistance of hydride electrode are 0.30 Ω, 0.24 Ω and 0.15 Ω respectively corresponding to dry method, wet method and wet method with additive.

降低电极电化学反应电阻，采用干法、湿法或湿法加添加剂制粉工艺贮氢电极的反应电阻分别为030Ω、024Ω和015Ω；

Electrochemical impedance spectra ( EIS) measurements revealed that with the DOL pretreatment lithium electrode had lower and more stable interface resistance during the storage in electrolyte for a long time.

电化学阻抗谱（EIS）分析表明，当金属锂电极长时间浸泡在电解液中时，经过DOL预处理的锂电极与未经处理的锂电极相比，具有更低、更稳定界面阻抗。

The model contains ohm resistance, a constant phase angle element ( CPE) standing for double electrical layer on porous electrode, charge transfer resistance and Warburg resistance.

模型包含欧姆阻抗、多孔电极双电层的恒相位元、电荷传递阻抗和Warburg阻抗。