The bond exhibited typical glass phase with low melting temperature and high bending strength of strips ( 53.62-93.34MPa). The microstructure analysis indicated the enhancement of the bonding strength resulted from the chemical reaction between the vitrified bond and microcrystal alumina ceramic.

结合剂为典型玻璃相，熔融温度较低，试样抗折强度为53.62-93.34MPa，微观分析表明两者间发生了化学反应，增强了结合剂对磨粒的把持力，提高了磨具的强度。

Application of VN alloy in 400? Mpa-grade reinforced bar

氮化钒合金在400MPa级钢筋中的应用

Level shearing strength should be more than 3 MPa.

水平剪切强度应≥3MPa；

μ m, the slenderness ratio of less than 2 ∶ 1, the single particle of water and gypsum ratio is 0.22 and 3-days compression strength reached 61.1? MPa of alpha hemihydrated gypsum.

制备了二轴平均径12.5μm、长径比2∶1、单一粒径水膏比0.223、d抗压强度达到61.1MPa的α半水石膏。

On the other hand, simulate by the Fluent software the jetting status of the double orbits water jet spiral nozzle jetting under 40 MPa pressure-inlet, then got the best working status of the spiral cone jet nozzle.

另外还用Fluent软件分别对双头不同导程的2种旋转喷头在40MPa进口压力条件下的喷射状态进行分析，从而得出旋转锥形喷嘴的最佳工作状态。

In producing high performance prestressed hollow slab, cold rolled rib steel and cold drawing grade ⅱ, grade ⅳ steel were replaced by 1270~ 1570 MPa mid-high strength spiral wire as prestressed reinforcement for hollow slab.

以强度为1270～1570MPa的中高强螺旋肋钢丝代换冷轧带肋钢筋及冷拉Ⅱ级、Ⅳ级钢筋作短向和长向圆孔板的预应力配筋，试生产高效预应力构件已获得成功。

A gold film was evaporated onto the fresh surface of mica. By immersing the gold film in the mercaptopropionic acid ( MPA) solution, Au S bond was formed between Au and the hydrosulfide group.

在新鲜裂解的云母表面镀一层金膜，金膜与疏基丙酸（MPA）的疏基形成S－Au键。

During the three experiments separately performed, through nozzles SF6 gas was sprayed at a pressure difference of 0.06 MPa into an air-tight molten pool reactor of 430 ℃ initial temperature containing liquid-state metal lithium.

在分别进行的3个实验中，将压差为0.06MPa的六氟化硫气体经喷嘴喷入装有液态金属锂，初温为430℃的密闭熔池反应器内。

The bending strength of this slide plate is up to 48.7 MPa at 1400 ℃, and its service life is two times as that of Al2O3?

Al2O3滑板材料，其1400℃高温抗折强度高达48.7MPa。

The rupture process and instability mode of step-like asperity located on sliding plane in granite specimen were studied under triaxial compression at confining pressures of 300-500 MPa.

本文介绍了三轴压缩下花岗岩试件内阶梯形错动面凸起部位破裂过程和失稳型式的实验。

The results show that face opening force, film stiffness and leakage rate are strongly affected by the slip flow under the operating conditions of low sealing pressure and low speed, especially when the pressure is between 0.152 MPa and 0.303 MPa.

结果表明，在低速和低压条件下，密封的端面开启力、气膜刚度和泄漏量均受到滑移流的显著影响，其中当密封压力为0.152~0.303MPa时影响最显著。

Super critical light water cooled reactor ( SCWR) is a high temperature, high pressure water cooled reactor, which can operate above the state of the thermodynamic critical point of water ( 374 ℃, 22.1 MPa).

超临界水冷却反应堆（SCLWR-H）系统是一种高温高压的水冷反应堆，它可以在高于水的热力学临界点（374℃，22.1MPa）的工况下运行。

Saturated properties tables covering the temperature range of-80~ 100 degree centigrade and the pressure range of 10 kPa~ 3 MPa were listed with the temperature and pressure basis, respectively.

在以温度和压力为基准的饱和性质表中，列出了温度在-80℃～100℃、压力在10kPa～3MPa之间，该混合工质的饱和热力性质。

Effect of 0.5 MPa hyperbaric oxygen exposure on GAD content in cultured neurons

0.5MPa高压氧暴露对培养的神经元中谷氨酸脱羧酶含量的影响

mpa has no effect on lipids metabolism, whereas ce plus mpa can improve the profile of lipids composition, which might be beneficial for the cardiovascular system.

MPA对血脂代谢无明显影响，CE加MPA可以改善血脂构成，使其有利于心血管系统。

High pressure water mist sprayer in order to realize the good atomization, the spray pressure must be to 7 MPa or above. After the pressure increase to 10 MPa, the fire fighting efficiency will get more improved.

高压细水雾喷头要实现良好雾化，喷雾压力必须在7MPa以上；但压力提高到10MPa后，细水雾的灭火效率才得到更大的提高。

pitch fluoride was prepared through mesophase pitch grain reacted with fluorine gas in rotative nickel reactor. gas pressure was up to 0.10mpa; reaction temperature was kept at range from 80 ℃ to 90 ℃.

在旋转式反应釜中采用中间相沥青微粒与氟气进行反应（反应条件：气压0.10MPa；温度80~90℃）制备出氟化沥青。

According to the maximum pressure to bear, pump body and cover can be made of grey cast iron ( 1.6Mpa), spheroidal graphite cast iron ( 2.0Mpa) or cast steel ( 2.5Mpa, including stainless steel).

根据泵承受的最大压力，泵体和泵盖材质采用灰口铸铁（1.6Mpa）、球墨铸铁（2.0Mpa）、铸钢（2.5Mpa，包括不锈钢）。

The flexural strength of materials reaches 100 MPa after the hydrolyzing resistance test.

经耐水解性试验后，材料的弯曲强度保持在100MPa以上。

This cooling method will get the yield strength of 435 MPa and tensile strength of 540 MPa, elongation of 30% of the high-intensity, and good toughness of low-carbon automobile beam steel, which can satisfy the need of users.

能得到屈服强度为435MPa，抗拉强度为540MPa，延伸率为30%的强度高、韧性好的低碳汽车大梁钢。